General-purpose low-carbon steel wire.
Heat treated. Without coating.
Chemical composition, %: С=0.06-0.12, Si≤0.05, Mn=0.25-0.5, S≤0.05, P≤0.04.
Breaking strength, Kgf: 290-490.

General-purpose low-carbon steel wire. Not heat treated. Galvanized.
Chemical composition, %: С=0.06-0.12, Si≤0.05, Mn=0.25-0.5, S≤0.05, P≤0.04.
Breaking strength, kgf: 560-900.

General-purpose low-carbon steel wire. Not heat treated.
Chemical composition, %: С=0.06-0.12, Si≤0.05, Mn=0.25-0.5, S≤0.05, P≤0.04.
Deviation from nominal diameter:

Low carbon hot dipped steel wire. Heat-treated. Galvanized.
Zinc coating: ≥ 40 gr/m2
Carbon content: 0.06-0.1%
Tensile strength: 340-520 N/mm2
Common packing 20-70 kgs/coil
Steel boiling.
The absence of a wire rust, oxides, grease, after drawing.
Coil with two ends (one-piece wire)
Welding points should be treated (welding joint, processed core welding)
0.7mm +/- 0.05mm, 0.8mm +/- 0.05mm