| Flux Content: | 25% |
|---|---|
| Application: | Use for building, machinery,metallurgy,pipeline etc. |
| Weight: | 5kg |
| Diameter: | 0.6-2.0mm |
| Material: | low carbon steel |
| Model Number: | E70T-5 |
| Brand Name: | Zander or OEM |
| Place of Origin: | China (Mainland) |
| Packaging: | 1kg/D100,5kg/D200,15kg/D270 |
Quick Details
Specifications
E70T-5 Flux cored welding wire
Specifications
1.low splashing
2.stability of arc
3.welds all position
4.the best price
Packaging & Delivery
|
Packaging Detail: |
5kg/spool,standard package or as your request |
|
Delivery Detail: |
10-15days after received your deposit |
The chemical analysis of deposited metal(%):
|
Chemcal analysis |
C |
Si |
Mn |
P |
S |
|
Typical |
0.06 |
0.44 |
1.42 |
0.015 |
0.010 |
|
Specification |
≤0.18 |
≤0.90 |
≤1.75 |
≤0.03 |
≤0.03 |
Mechanical properties of deposited metal:
|
Mechanical properties |
Yield point (Mpa) |
Tensile Strength (Mpa) |
Elongation (%) |
Charpy V-notch Impact Value(J) |
|
|
Typical |
551 |
598 |
30 |
-20°C |
119 |
|
Specification |
≥375 |
490-660 |
≥22 |
47 |
|
Welding detais:
|
Diameter |
1.2mm |
1.4mm |
1.6mm |
|
|
Welding Current (A) |
Flat welding |
120-300 |
160-400 |
190-450 |
|
Flat fillet welding |
120-300 |
460-350 |
190-400 |
|
|
Horizontal welding |
120-280 |
150-320 |
180-350 |
|
|
Verticaldownwelding,overhead welding |
120-60 |
160-320 |
180-280 |
|
|
Vertical down welding |
200-300 |
220-320 |
250-300 |
|
Application:
Used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels, boilers, petroleum machinery, chemical machinery, hoisting machinery, etc.
Detailed description:
It is a kind of gas-shielded flux-cored welding wire for low-carbon steel and 490MPa high strength steel. And it is a kind of titania type CO2 gas-shielded flux-cored welding wire. Suitable for downhand welding and horizontal welding. It has high welding efficiency. The weld metal has been given toughening treatment by microelements, so it has excellent low temperature toughness, good crack-resistance and stable and reliable inherent quality.