Material: | 60Si2MnA, 60Si2CrA, 55Si2Mn, 38Si7 |
---|---|
Surface: | Bluing, Plain Oiled, Color Painting, HDG, etc. |
Hardness: | 44-48HRC |
Standard: | DIN17221, BS970, GB/T1222 |
Fatigue life: | 5 Million Times without Crack |
Partnership: | Agents, Distributors are welcome |
Quality Control: | Inspection on each workshift/new batch material/machine adjustment |
Manufacturer: | Kunshan Alex |
Quick Details
Specifications
Technical Parameter of The E Clip
Diameter (mm) |
Weight (Kg) |
Toe Load (Kgf) |
12 |
0.18 |
200~400 |
14 |
0.30 |
400~600 |
16 |
0.44 |
500~700 |
18 |
0.59 |
800~1000 |
20 |
0.76 |
1100~1400 |
Material:
60Si2MnA
Fatigue Property: When spring deflection is 9.1mm, fatigue life is up to 5
million cycles without breaking.
Material Reference: DIN 17221, BS970, GB/T 4357, GB/T 4358.
Clamping force 25KN, Fatigue life 3 millions to 5 million
Clip Toe Deflection |
Toe Load Range |
10.5mm~14.5mm |
1100Kgf~1400Kgf |
11mm~14mm |
800Kgf~1000Kgf |
14mm~15mm |
650Kgf~750Kgf |
Surface: Plain with anti-rust oil, Bluing (Black Oxide), Painting, Zinc Plating or as per requirement.
MOQ: 5000pcs
Packaging: 15pcs or 50pcs per woven bag. Fumigation free Pallet. Clients can appoint the way.
We are a leading elastic rail clip manufacturer in China. We can also make other rail fastenings such as railway screw, plastic dowel, rail pad, railway insulator, rail fish bolt, railway base plate, rail anchor, railway shoulder, rail bolt, flat and spring washer, fastening system of E type/SKL type/KP type/Nabla type.
2> SKL Clip
Technical Parameter of The E Clip
Diameter |
Type |
Weight (Kg) |
13mm |
SKL1 |
0.49 |
13mm |
SKL3 |
0.53 |
13mm |
SKL12 |
0.53 |
13mm |
SKL14 |
0.505 |
Material:
60Si2CrA
Loading Property: Under pressure 8-12KN, the displacement is between 9-12mm.
Fatigue Property: No less than 5 million times.
3> PR Clip
Technical Parameter of The PR Clip
Material |
60Si2MnA |
Bar Diameter |
7/8" |
Nominal Toe Load |
2,000 lbs |
Nominal Rail Seat Clamping Force |
4,000 lbs |
Working Deflection |
0.56" |
Weight |
2.75 lbs |
4> Nabla Clip
Material |
60Si2MnA |
Loading Property |
2500DaN |
Hardness |
HRC51~55 |
After the first two tests, variation of the height after releasing is only 0.45mm and after three more tests, there is only 0.1mm variation of height
5> Vertical Special Rail Clip
Material |
60Si2MnA |
Loading Property |
2500DaN |
Hardness |
HRC51~55 |
6> Rail Deenik Clip
Material |
60Si2MnA |
Diameter |
16mm |
Hardness |
HRC51~55 |