Packing specification of BD766 anti wear anti corrosive high temperature resistant coatings:
25 Kg/group, packed in a plastic drum or iron drum.

performance feature of BD766 high temperature anti corrosion abrasion resistant coating:
1. Excellent in wear & corrosion resistance                               
2. With very high bonding strength to metal substrates              
3. Convenient for construction,without very high technical requirements for constructors         
4.Suitable for the protecting of high temperature wear working condition          
5.Can do blade coating directly for both facade and ceiling,don't drip and slip,without the support

product usage of BD766 wear resistant high temperature corrosion resistant coatings:
   Two component,fine particle,room temperature curing,wear resistant,the highest temperature resistant is 600℃,used in the wear resistance of flue

performance index:

BD766 high temperature wear resistant coatings  performance index
product name	physical state	color	operational time limit(25℃)	can put into using time(25℃)
BD766 high temperature wear resistant coatings	paste	yellow	40min	7d

BD766  Physical mechanical properties table
density (g/cm3)	compressive strength(kg/cm2)GB1041-2008	tensile strength (kg/cm2)GB6329-2009	shear strength(kg/cm2)GB7124-2008	-	hardness(ShoreD) ASTM-D-255	working temperature of ensuring wear resistance(℃)
2.1	650		40	-		-60～600

How to use of BD181 anti abrasion corrosion resistant coating:
1.  Surface treatment:Do coarsening treatment on the pending-repair part,grinding with angle grinder or sand blasting etc,the surface after coarsening treatment should be cleaned,the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no greasy dirt and dust.
2.   Preparation:According to weight ratio A:B=4:1,make A and B two components mix uniformly,and use it up within 40 min.Generally it's while construction and configuration.Every time the most configuration quantity is not more than 20Kg,too much adhesive is solidified too fast,hasn't been used up until the adhesive has partial solidified and can't be used.According to the actual temperature,configuration can be properly a little more in winter and proper less in summer.
3.  Coating:The suitable coating thickness of  BD766 high temperature wear resistant coatings  is 1-4mm.Make the mixed-up material be coating on the pending-repair part layer by layer,the first layer should be compacted,make it infiltrates fully with the substrates.The thickness of each layer should be controlled under 0.5－1mm,spread coating the next layer after the upper layer drying,the application time of coating for two successive is depend on the construction temperature and coating thickness,it's more than 10 hours in winter based on 0.5mm coating thickness,but more than 4 hours in summer.The principle which we should grasp is that coating on the next layer after the upper layer drying.
4.  Curing:After the coacting is coated in the specified size,generally we need to place it for 2-3 days before putting into use.

Transportation storage:
1.Sealed storage in the cool and dry place,the warranty period is 1 year.
2.Avoid placing it upside down,knocking against and transporting it as a non-dangerous product during transportation.