Technique: | Hot Rolled |
---|---|
Type: | Steel Plate |
Brand Name: | shangyi |
Thickness: | 6mm |
Standard: | AISI,ASTM,BS,DIN,GB,JIS |
Length: | 5800 |
Width: | 2000 |
Special Use: | Wear Resistant Steel |
Application: | Flange Plate |
Surface Treatment: | Coated |
Model Number: | Mn13 |
Place of Origin: | China (Mainland) |
Grade: | mn13 |
Quick Details
Specifications
the following example is for you reference.
Main Advantages:
Mn13 is kind of high manganese wear- resistant steel material, which is the best choice for resisting high impacts, high pressures among wear- resistant steels. the features of Mn13 steel plates: 1. the heavier the impacts from outside to the surface of steel plates, the higher performance of abrasive resistance from surface of steel plates will have. 2. with the abrasion of hardening layer of Mn13 steel plates, more new hardening layers will be taken shape continually. Mn13 hot rolled steel plates have excellent properties in resisting strong impacts abrasion and high stress abrasion. Besides, Mn13 steel plates won't be crushed when in application and are easy to be cutted, welded and bended when taking mechanical machining works.
Application:
Mn13 steel plates are widely used in liners of ball mill, excavator dipper teeth, dental plates of crusher machine, safe case, bullet- proof car, etc. Normally Ma13 steel plates are popular in the applications with easy structure like liner plates, teeth plates, broken walls, rolling ace tabular wall, roller shell, form relieved teeth, etc.
Technical Details:
Heat Treatment: Normalized, Quenched, Tempered, HIC, Impact Test,..( Optional if not provided in rules)
Chemical Composition( %):
Grade/ Material-----Mn13
Element-----Composition( Max-A, Min-I)
C-----A:0.90-1.20
Mn-----A:11-14
Si-----A: 0.30-0.80
P-----A:0.035
S-----A:0.030
Mechanical Properties( Mpa)
Grade/ Material-----Mn13
Tensile Test-----MPa
Tensile Strength-----I:800
Yield Strength-----I:--
Elongation-----I:40%
Impact Test( if any)-----0℃
HB-----I:300