The product is suitable for large blast furnace ceramic cup,blast tuyere,

iron notch and slag notch,which has achieved good application results at 

Wuhan I&S Corp.(for 3200m3 blast furnace),

Tianjin Tiangang Steel Group(for 2000m3 blast furnace),

Liuzhou Iron&Steel Co.,LTD(for 1260m3 blast furnace),

Hangzhou Iron&Steel Group Co.(for 497m3 blast furnace).

 

Typical technical specification:

Model:WGZ-2

AL2O3: Min85%

Fe2O3 : Max0.8%

Bulk density:Min3.20g/cm3

Apparent porosity:Max14%

Cold crushing strength:Min160MPa

Air permeability:Max0.5mDa

Corrosion index to hot metal:Max1.0%

Corrosion resistance to slag:Max6%

Average pore size:Max0.3micron

<1micron pore volume:Min75%

Thermal conductivity(600C):Max5W/m.k

Corrosion resistance to alkaline:Excellent,no cracks