The  product  is  made  of  fused  brown  corundum  and  silicon  carbide  as  starting  materials,   added  with  special  additives,   through  mould  press  process  and  sintering  before  fine  machining,   The  refractory  brick  is  characterized  by  good  alkaline  resistance  and  slag  corrosion  resistance,   which  is  suitable  for  lining  the  bottom,hearth  ceramic  cup,   tuyere,   iron  notch  and  slag  notch.   and  exported  to  Yenakiyeve/Ukraine, ZS/Russia,   Bhushan/India  etc.

 

Typical  technical  specification:  

Al2O3: Min78% 

SiC: Min14% 

Fe2O3  :Max1. 0% 

Bulk  density: Min2. 9g/cm3 

Apparent  porosity  :Max15% 

Cold  crushing  strength: Min100MPa 

RUL  at  0. 2MPa: Min1660C 

Permanent  linear  change  (1500C*3h): 0-0. 2%

Thermal  expansion(1000C): 0-0. 5%

Corrosion  resistance  to  slag: Max10%

CCS  after  alkaline  corrosion  test: Min70MPa