Features
Good heat-durability, Low temperature coefficient, low noise, high load power, high insulating capacity, nonflammability. |
|
Note: The sleeve must be totally inside the ceramic. Cement must be totally inside the ceramic |
II. MATERIALS
|
Resistor ceramic nucleus |
S-75 ceramic rod |
|
|
|
Cap |
Tinned sealed copper |
Terminal |
Annealed |
|
Ceramic cage |
Ceramic Steatite |
Coating depostion |
Metal oxide fired at high temperature |
|
Silicon Fiberglass Sleeve |
UL Approved |
Coating material |
Metal oxide film resistor |
|
As Alternative: Silicon Sleeve |
φint 1mm 4000V Wallthick: 0.5mm |
|
|
|
As Alternative: Silicon Sleeve |
φint 1mm 4000V Wallthick: 0.5mm |
COLOR:White |
JIS-5202 standard : 250 ppm/Max |
III.PRODUCTION CHARACTERISTICS
|
Ohmic Value |
22Kohm +/- 5% |
Terminal length |
See Drawing |
|
Resistor pre-value |
|
Terminal diameter |
0.8mm |
|
Resistor length |
see drawing |
Terminal projection |
See Drawing |
|
Resistor diameter |
see drawing |
Resistor winding |
Minium 70% of the total length (16.8mm) |
|
Resistor height from the bot |
0 mm |
Cement colour |
Grey-white (homogeneous colour) |
|
Cap length |
2.3+/- 0.1 mm |
|
|
|
Nacked Resistor Wattage |
5W |
|
|
IV. Supplier Checks
|
Overload test |
5 Seconds on naked pcs (2.5 *voltage*2W) |
5 seconds on fished product pcs (2.5 *voltage *5W) |
|
Ohmic Value |
100% check after overload test on Nacked part | |
|
Demensions:A,B,C, AQL0, 065 |
| |
|
A=9.3 +/- 0.2 B=9.7 +/- 0.25 C=22.2 +/-0.3 |
Caliper | |