Description
A porous alumina ceramic of 99.7% Al2O3 content, used extensively for long-life laser reflectors. This material is sintered at high temperatures to achieve a controlled porosity.
Prime features
-
Surfaces can be sealed and coated with a solarization-resistant glaze to give high bulk refectivity
-
97.8% reflectance efficiency at 1000nm
-
Reflectance efficiency exceeds 96% across the wavelength range 500-2000nm (see curve)
-
Controlled porosity
-
Good thermal conductivity
-
High electrical resistivity
Typical applications
Pumping chambers for Nd:YAG lasers — low to high power, single or multiple lamp designs. Pumping chamber reflectors of this material are virtually indestructible, and prove a highly cost effective alternative to metal coated types.
Specifications
Quality Assurance to BS EN 9001:2000
Production capabilities
-
Components up to 250mm long and 80mm wide/diameter manufactured as standard
-
Larger components manufactured to development contracts
-
One-piece or split-cavity designs
-
Prototype, batch and volume production.
Physical properties*
Color: White
Bulk density (fired), Mg/m3 :3.2
Porosity (apparent), % nominal :20
Flexural strength (ASTM C1161, 3-point), MPa :150
Thermal expansion coefficient
200-500C, 10-6/C 7.9
200-1000C, 10-6/C 9.0