Product name |
High temperature resistant magnetic steel adhesives（THO4058） |
Outline |
Being high temperature resistant and age resistant, this double-component product is acrylic acid polyester adhesive. It is easy and convenient to use for it solidifies fast at normal temperature and bonds well. |
Applications |
This product is widely applied to the self-adhesion and mutual-adhesion of such materials as motor magnetic ring (magnetic coil), magnetic metal,ceramics and composite materials. It also applies to the bonding, sealing, filling, repairing and stopping of cracks between the materials as magnetic and steel and the magnet. |
Features |
The A component is the tinted thick liquid, non-solid particle. The B component is in tinted paste shape. Fast curing velocity. At 25℃, 1-3 hour it is at the early stage of curing, 18 hours later, it reaches its maximum bonding strength. It cures during 40-60 minutes if put into heating oven of 80-100 ℃ Being durable and resistant to ultraviolet light, once the bond has formed. Being heat-resistant, it adapts to a wide range of temperature and bonds well under high temperature. With moderate viscosity, the adhesive leaves no bubbles, making the surface smooth and bright. Mix the two components in a certain proportion, apply it to the surface of the substrates directly, which makes it so convenient to use. You'll see long term durability and resistance to moisture, chemicals, oils, and temperature extremes. Non-toxic after solidification, though it is a little smelly. Being stable, its storage time is one and a half year. The main technical performance indicators are as follows: Heat resistance scope：-45－+410℃
Cementation intensity: Normal temperature: Tensile strength≥25MPa; Shearing strength≥23 MPa
150℃: Tensile strength 3-4.5 MPa |
Instruction |
1. Clean the surface of the material, make sure they have no dust or oil on them, wait until they are dry. 2. Mix A and B in a proportion of 10: 1.2--1.5 to get perfect bonding result at fastest speed at 25 C. 3. Spread the mixture on the substrates, put them together and apply some strength on them, finally, let them dry for 2-4 hours. 4. If the surface of ceramics needs to be shaped after the coating, hot press molding or cold press molding should be applied when the adhesive is in its preliminary curing time. |
Notes |
1.The tools used to get adhesives should have exclusive usage. 2. It is necessary to keep it well ventilated and away from fire . 3.If it has contact with skin, you should wash with soapy water. 4. It can be stored at well-ventilated places with low temperature, and keep them away from fire. Cover the lip after using it. |