KAOLIN for CERAMICS

ROW CLAY：

RTC-RC:% Particles < 2 μm：≥45.0 pH：4~6 SiO2：68 Al2O3：≥22.0

Fe2O3：≤1.2 TiO2：≤0.2 Brightness after firing：60-70 Moisture%：30/15

Traits：high plasticity， high caking property，high strength

WASH KAOLIN

RTC-90:% Particles < 2 μm：≥40 pH：2.5 SiO2：48 Al2O3：≥38 Fe2O3：0.50

TiO2：≤0.2 Brightness after firing：89-90 Moisture %：28±2

Traits：high brightness

RTC-86:%Particles<2 μm：≥50.0 pH：4~6 SiO2：50 Al2O3：≥36.0

Fe2O3：≤0.80 TiO2：≤0.2 Brightness after firing：86-87 Moisture%：28±2

Traits：high brightness

RTC-83:% Particles < 2 μm：≥45.0 pH：4~6 SiO2：50 Al2O3：≥35.0

Fe2O3：≤0.85 TiO2： ≤0.2 Brightness after firing：83-85 Moisture%：28±2

Traits：high brightness

RTC-81:% Particles <2μm：≥40 pH：4~6 SiO2：50 Al2O3：≥34

Fe2O3：≤0.95 TiO2：≤0.2 Brightness after firing：80-83 Moisture%：28±2

Traits：high brightness

RTC-78:% Particles < 2 μm：≥35 pH：4~6 SiO2：50 Al2O3：≥33

Fe2O3：≤1.1 TiO2：≤0.2 Brightness after firing：76-80 Moisture%：28±2

Traits：high brightness

RTC-74:% Particles < 2 μm：≥30 pH：4~6 SiO2：50 Al2O3：≥32

Fe2O3：≤1.2 TiO2：≤0.2 Brightness after firing：72-76 Moisture%：28±2

Traits：high brightness