Structure |
All-glass double-tube co-axial structure |
Glass material |
High borosilicate 3.3 glass |
External pipe diameter and thickness |
Φ=47±0.7mm &=1.6mm Φ=58±0.7mm &=1.6mm Φ=70±0.7mm &=2.0mm |
Internal pipe diameter and thickness |
Φ=37±0.7mm &=1.6mm Φ=47±0.7mm &=1.6mm Φ=58±0.7mm &=1.6mm |
Pipe length |
800mm 1200mm 1500mm 1600mm 1800mm 1900mm 2000mm 2100mm |
Absorbing coating property |
Structure |
|
Sediment method |
|
Spectific absorption |
|
Emission ratio |
|
|
AL/AL-ALN(H)/AL-ALN(L)/ALN
|
Single target magnertron sputtering plating |
as=0.90~0.93(AM1.5)
|
εh=0.05~0.075(80℃±5℃) |
|
Vacuum tightness |
P≤5.0X10-3Pa |
Idle sunning property parameters |
Y=220~260m2.℃/KW |
Solar irradiation for obtaining a preset water temperature |
H≤4.7MJ/m2(Φ58) |
|
H≤3.7MJ/m2(Φ47) |
|
|
H=4.1~4.4MJ/m2
|
H=3.1~3.4MJ/m2 |
|
Average heat loss coefficient |
ULT=0.6~0.7W/(m2.℃) |