Product Main

Specifications

Super-X No.8008

Cemedine Super-X is an epoch-making one-part quick curing adhesive having three significant features which are said to be ideal properties of the adhesives; "pressure-sensitive adhesion", "elastic adhesion" and "solventless adhesion".

Features

1. Pressure-sensitive adhesion Curing reaction is caused by moisture absorbed from the air. Pressure-sensitive range is reached in this curing process about 10 min. after application. If adherends are put together during this time, they bound instantaneously as in the case of rubber contact adhesive, eliminating the need for temporary fixation.
2. One-part solventless agent providing quick curing at normal temperature Easy-to-use, safe, and clean adhesive featuring one-part solventless agent capable of quick curing at normal temperature is provided.
3. Adhesive property over an extensive range Super-X products allow for adhesion of various types of plastics, rubbers and ceramics over an extensive range, moreover different types of metals. These products provides excellent adhesion over a very extensive range of materials, eliminating the need for selecting a particular adhesive for each type of the different materials, as in the case of conventional agents.
4. Durability The Super-X as elastic adhesives do not peel off. Once materials are adhered, the Super-X provides durability in the range from low temperature (-60°C) to high temperature (120°C). Because of the rubber state of the hard film, the Super-X follows the changes of adherents such as expansion and shrinkage sufficiently.
Super-X conceptual diagram

Application

? Adhesion required to have initial adhesive strength ? Adhesion of different types of materials having different thermal expansion coefficients
? Adhesion required to have durability due to repeated heating, cooling and vibration ? Electrical contact failure countermeasure product
Adhesive strength for various types of adherends
Classification Adherend Tensile shear adhesive strength after 7-day curing (N/mm2)
Open time, 3 min. Open time, 25 min.
Metal Steel plate (SPCC, SPCD) 3.92 3.92
Aluminum (*1) 4.21 4.12
Stainless steel 4.21 3.92
Copper 4.51 4.21
Plastics Polycarbonate 4.31 3.23
Bakelite 4.21 54.02
ABS 2.45 1.96
Plasticized polyvinylchloride 3.92 3.14
Styrene 2.74 2.25
Acryl 2.94 2.16
6-nylon 2.84 2.65
FRP (*2) 4.02 2.94
Polyethylene foam (*3) 0.98 -
Polypropylene (*4) 2.45 -
PEEK (polyether ketone) 3.14 -
PES (polyether sulfone) 3.82 -
PSF (polysulfone) 3.53 -
PET (polyethyleneterephthlate) 1.67 -
PPS (polyphenylene sulfide) 3.72 -
PPO (polyphenylene oxide) 4.41 -
PAR (polyarylate) 4.12 -
Oxybenzoyl polyester 2.25 -
Others Slate 1.86 1.67
Plywood 2.65 3.14

Conditions: Coated on both sides, 50μm thick (one side), tension speed between adherends: 50mm/min.

Note:
*1 and *2: Surface preparation will cause adhesive strength to become uneven; it must be confirmed in advance.
*3: Surface preparation by exposure to ultraviolet ray.
*4: Primer (Cemedine PP-5) to be used.
Adhesive strength for various types of rubbers
Classification Adherent Peeling adhesive strength
after 7-day curing (N/mm)
Rubber Natural rubber 0.88 Substrate failure
NBR 2.36 Cohesion failure
Silicone rubber 0.84 Substrate failure
SBR 2.36 Substrate failure
EPDM 0.80 Adhesion failure
EPDM (*) 2.36 Cohesion failure
Chloroprene rubber (CR) (*) 0.72 Adhesion failure
CSM (chlorosulfuric oilyethylene) (*) 0.56 Adhesion failure

(*): Degreasing by toluene after treatment by sand paper (#120).

Chemicals resistance
Chemicals Tensile shear strength after dipping in chemicals (N/mm2)
Unprepared 4.31
Water 3.63
Acetic acid (1% water solution) 3.72
Acetic acid (10% water solution) 1.96
Sulfuric acid (3% water solution) 4.41
Sulfuric acid (30% water solution) 4.02
Sodium hydroxide (1% water solution) 4.41
Sodium hydroxide (10% water solution) 4.51
Machine oil (Idemitsu: Mechanic Oil) 4.21
Salt (10% water solution) 4.31
Methylethylketone (*) 0.29
n-hexane (*) 0.78

(Conditions): Coated on both sides, 50μm thick (one side), open time 3 min.
Stainless steel and stainless steel Pressing: one day for clip Curing: 7 days
Number of days to be dipped in chemicals: 7 Tensile speed: 50mm/min.
* Deterioration of solvent is observed, but no problem with short-time contact, for example, in washing.

Initial curing speed

Tensile shear adhesive strength, after repeated heating and cooling

Tensile shear strength on each temp

Tensile shear adhesive strength after heat aging

List of Super X Adhesives
Product name Super X No.8008 Super X No.8008 black Super X No.8008 clear Super XL black
Main component Special polymer
containing silyl group
Special polymer
containing silyl group
Special polymer
containing silyl group
Special polymer
containing silyl group
Appearance White paste Black paste Light yellow
translucent paste
Black paste
Viscosity (Pa?s/23°C) 90 90 65 24
Specific gravity (g/cm3) 1.26 1.26 1.07 1.24
Tack free time 11 11 8 11
Tensile shear adhesive strength (N/mm2) 3.7 3.7 3.4 3.2
T type peeling adhesive strength (N/mm) 2.5 2.5 1.7 2.4
Curing
properties
Hardness (Shore A) 42 42 45 31
Glass transfer point (°C) -63 -63 -64 -68
Breaking strength (N/ mm2) 1.8 1.8 1.6 0.9
Breaking extension (%) 220 220 150 300
Linear expansion coefficient 2.1×10-4 2.1×10-4 1.8×10-4 2.4×10-4
Electric
characteristics
Volume resistivity (Ω?cm) 2.0×1011 2.0×1011 9.0×1011 5.0×1011
Dielectric constant (100Hz) 0.2 0.2 0.2 0.2
Dielectric loss tangent (100Hz) 0.03 0.03 0.10 0.06
Formaldehyde grade
Capacity standards 170g 333ml 170g 333ml 333ml 170g 333ml

 

Adhesive for electrical components SX720 (W, WH, B, and BH)

  1. Nonflammable product (UL94V-0 listed). (File No.E178790)
  2. One-part elastic adhesive capable of curing at normal temperature and humidity.
  3. Quick initial adhesion, high tack power for various types of materials, and excellent durability.
  4. Safe and global environment-friendly adhesive.
  5. Electrical contact failure countermeasure product.
  • Contains no low molecular siloxane component.
  • Employs no halogen-based, antimony oxide, or phosphorus-based materials.
  • Employs no volatile solvents.
Application

? Fixing of circuit boards such as condenser and coil ? Sealing of power supply and transformer for insulation
? Sealing of electronic components for waterproofing  
List of SX720 Adhesives
Product name SX720W SX720WH SX720B SX720BH
Main component Special polymer
containing silyl group
Special polymer
containing silyl group
Special polymer
containing silyl group
Special polymer
containing silyl group
External appearance White paste White paste Black paste Black paste
Viscosity (Pa?s/23°C) 45 70 45 70
Specific gravity (g/cm3) 1.53 1.55 1.53 1.55
Tack free time 8 9 8 9
Tensile shear adhesive strength (N/mm2) 3.9 3.4 3.9 3.4
T type peeling adhesive strength (N/mm) 1.4 1.3 1.4 1.3
Curing
properties
Hardness (Shore A) 62 66 62 66
Glass transfer point (°C) -67 -65 -67 -65
Breaking strength (N/mm2) 2.4 2.1 2.4 2.1
Breaking extension (%) 175 170 175 170
Linear expansion coefficient 1.1×10-4 1.1×10-4 1.2×10-4 1.2×10-4
Electric
characteristics
Volume resistivity (Ω?cm) 2.0×1011 2.0×1011 2.0×1011 2.0×1011
Dielectric constant (100Hz) 0.3 0.3 0.4 0.4
Dielectric loss tangent (100Hz) 0.11 0.32 0.12 0.32
Thermal conductivity (W/m?k) 0.97 0.99 0.97 0.99
Capacity standards 200g
333ml
200g
333ml
200g
333ml
200g
333ml