Stainless steel welding electrode are used for welding corrosion-resistant stainless steel structures of ocr19ni11ti under 300.
Features:
1) welding temperature is lower than 300 degrees.
2) stainless steel structure. Inner packing
1) 2.5mm x 300mm, 1-5kg/inner box + plastic bag.
2) 3.2mm x 350mm, 1-5kg/inner box + plastic bag.
3) 4.0mm x 350mm, 1-5kg/inner box + plastic bag. Chemical composition %. C. Mn. Si. Cr. Ni. Cu. Mo. S. P. Standard value. =0.04.0.5-2.5. =0.09.17.0-20.0.11.0-14.0. =0.75.2.0-3.0. =0.030. =0.040. Example value. 0.030.0.85.0.62.19.00.11.86.0.16.2.50.0.012.0.028. Mechanical properties. Tensile strength(mpa). Elongation a (%). Standard value. =490. =30.
Example value. 575.44.
Range of current: (AC or DC+).
Diameter & length(mm). 2.5*300.3.2*350.4.0*350.5.0*350.
Range of current. Downward welding. 50-85.80-120.100-150.140-180. (amp). Overhead welding. 45-80.70-110.90-135.
| Type |
Model GB |
Chemical composition |
| C |
Mn |
Si |
S |
P |
Cr |
Ni |
Mo |
other |
| THA102 |
E308-16 |
0.08 |
0.5-2.5 |
0.90 |
0.030 |
0.040 |
18.0-21.0 |
9.0-11.0 |
0.75 |
Cu0.75 |
| THA112 |
-- |
0.12 |
2.50 |
1.50 |
0.035 |
0.040 |
17.0-22.0 |
7.0-11.0 |
-- |
-- |
| THA132 |
E347-16 |
0.08 |
0.5-2.5 |
0.90 |
0.030 |
0.040 |
18.0-21.0 |
9.0-11.0 |
0.75 |
Cu0.75 Nb8xC-1.00 |
| THA137 |
E347-15 |
0.08 |
0.5-2.5 |
0.90 |
0.030 |
0.035 |
18.0-21.0 |
9.0-11.0 |
0.75 |
Cu0.75
Nb8xC-1.00 |
| THA202 |
E316-16 |
0.08 |
0.5-2.5 |
0.09 |
0.030 |
0.040 |
17.0-20.0 |
11.0-14.0 |
2.0-3.0 |
- |
| THA302 |
E309-16 |
0.15 |
0.5-2.5 |
0.90 |
0.030 |
0.040 |
22.0-25.0 |
12.0-14.0 |
0.75 |
Cu0.75 |
| THA402 |
E310-16 |
0.08-0.20 |
1.0-2.5 |
0.75 |
0.030 |
0.030 |
25.0-28.0 |
20.0-22.5 |
0.75 |
Cu0.75 |
chemical composition / Mechanical properties/ Usage
| Type |
Model GB |
Mechanicl propertise |
| Rm(MPa) |
A(%) |
| THA102 |
E308-16 |
550 |
35 |
| THA112 |
-- |
540 |
25 |
| THA132 |
E347-16 |
520 |
25 |
| THA137 |
E347-15 |
520 |
25 |
| THA202 |
E316-16 |
520 |
30 |
| THA302 |
E309-16 |
550 |
25 |
| THA402 |
E310-16 |
550 |
25 |
Chemical composition / Mechanical properties / Usage
| Type |
Model(GB) |
Usage |
| THA102 |
E308-16 |
U sed for welding corrosion-resistant stainless steel structures of 0Cr19Ni0Cr18Ni11Ti under the temperatureof 300 degrees |
| THA112 |
— |
Used for welding corrosion-resistant stainless steelstructures of Cr18Ni19 |
| THA132 |
E347-16 |
Used for welding 0Cr20Ni11Ti stainless steel structures |
| THA137 |
E347-15 |
Used for welding 0Cr20Ni11Ti stainless steel structures |
| THA202 |
E316-16 |
Used for welding OCr17Ni12Mo2stainless steel suitablefor organic and inorganic acid medium |
| THA302 |
E309-16 |
Used for welding 0Cr21Ni10 and 0Cr17Ni12Mo2 stainless steel structures. |
| THA402 |
E310-16 |
Used for welding same kind of austenitic steel under high temperature.Also can be used for welding Cr5Mo,Cr9Mo,Cr13 stainless steel and different type of steel. |