Operation temperature: -50 to +125 Celsuis.
Security: used to protect switch systems up to 1kV and can reduce the distance to ground.
Convenience for application: the continous length as supplied make the application more conveniently and economically.
ZRG series products were recognized as jiangsu province high and new technical product in 2000, its product number:000500G0030N.
Security: used to protect switch systems up to 1kV and can reduce the distance to ground.
Convenience for application: the continous length as supplied make the application more conveniently and economically.
ZRG series products were recognized as jiangsu province high and new technical product in 2000, its product number:000500G0030N.
Specification:
1.Tensile Strength: ≥12 Mpa
2.Ultimate Elongation: ≥400%
3.Tensile Strength After Aging(After 7 Days Air Oven at 158Celsuis): ≥10 Mpa
4.Elongation After Aging(After 7 Days Air Oven at 158Celsuis):≥300%
5.Deformation Test(131Celsuis\1): ≤25%
6.Heat Shock @ 250Celsuis: No Cracking
7.Conductor Corrosion(After 7 Days Air Oven at 158Celsuis): No Corrosion
8.Volume Resistivity: ≥1014 Ω.cm
9.Dielectric Strength: ≥25 Kv/mm
10.Dielectric Withstand After Aging(After 7 Days Air Oven at 158Celsuis): 2.5Kv\60sec.
11.Breakdown Voltage After Aging(After 7 Days Air Oven at 158Celsuis): ≥12 Kv
12.Cold Bend(-30Celsuis\1hr): No Cracking
13.Longitudinal Change(200Celsuis\3minute): +10% to -10%
14.Eccentricity: ≤30%
15.Flammability: VW-1
1.Tensile Strength: ≥12 Mpa
2.Ultimate Elongation: ≥400%
3.Tensile Strength After Aging(After 7 Days Air Oven at 158Celsuis): ≥10 Mpa
4.Elongation After Aging(After 7 Days Air Oven at 158Celsuis):≥300%
5.Deformation Test(131Celsuis\1): ≤25%
6.Heat Shock @ 250Celsuis: No Cracking
7.Conductor Corrosion(After 7 Days Air Oven at 158Celsuis): No Corrosion
8.Volume Resistivity: ≥1014 Ω.cm
9.Dielectric Strength: ≥25 Kv/mm
10.Dielectric Withstand After Aging(After 7 Days Air Oven at 158Celsuis): 2.5Kv\60sec.
11.Breakdown Voltage After Aging(After 7 Days Air Oven at 158Celsuis): ≥12 Kv
12.Cold Bend(-30Celsuis\1hr): No Cracking
13.Longitudinal Change(200Celsuis\3minute): +10% to -10%
14.Eccentricity: ≤30%
15.Flammability: VW-1