Pure PTFE Packing is a braided packing made of pure PTFE thin yarns fiber, almost complete chemical inertia, dimensional stability, low friction coefficient to compression, and excellent. Resistance to compression are qualities classifying this packing among the best ones available in the industrial field. It is suitable for all the chemical compounds (excepting cast alkaline metals and the gaseous fluorine), alternative and rotary motions shafts operating at low peripheral speed, rods, pistons valve stems, expansion joints, etc. The Braided packing impregnated with PTFE are also available

Pressure	Mpa	2	10	20
Temperature	℃	<280
Linear speed	M/s	4	2	2
PH range		0~14
Size		3mm ~ 50mm

GP-1862 PTFE Packing with Oil Lubricant

Braided by PTFE fiber yarns and treated with a special inert lubricant .Under a minimum pressure of the stuffing box, it keeps unchanged in the long run. The low friction coefficient prevents the surface of the shaft from forming heat even in the presence of high peripheral speeds. GP-1862 Braided Packing is suitable for high-concentrated chemical products, strongly aggressive and oxidative Rubber core is also available.

Pressure	Mpa	2	10	20
Temperature	℃	<280
Linear speed	M/s	8	2	2
PH range		0~14
Size		3mm ~ 50mm

GP-1863 PTFE Fiber Packing with PTFE

Braided with PTFE filament, further impregnated piece by piece with PTFE dispersion. Features flexibility, almost complete chemical inertia, dimensional stability, low friction coefficient to compression, and excellent resistance to compression. Easily qualifies among the best packing available in the industrial field. It is suitable for all the chemical compounds (excepting cast alkaline metals and the gaseous fluorine), alternative and rotary motions shafts operating at high peripheral speed, rod, pistons, valve stems, expansion joints, etc.

Pressure	Mpa	5	15	25
Temperature	℃	-200~ 280
Linear speed	M/s	20
PH range		0~14
Size		3mm ~ 50mm

GP-1864 PTFE Fiber Packing with PTFE and Oil Lubricant

Braided with PTFE filament, further impregnated piece by piece with PTFE dispersion. Features flexibility, almost complete chemical inertia, dimensional stability, low friction coefficient to compression, and excellent resistance to compression. Easily qualifies among the best packing available in the industrial field. It is suitable for all the chemical compounds (excepting cast alkaline metals and the gaseous fluorine), alternative and rotary motions shafts operating at high peripheral speed, rod, pistons, valve stems, expansion joints, etc.

Pressure	Mpa	2	10	20
Temperature	℃	-200~ 280
Linear speed	M/s	20
PH range		0~14
Size		3mm ~ 50mm