Adhesion strength, high transparency, high-temperature cooking, and dry compound with good adhesion to polyurethane adhesive, after printing compound, fastness strong, high temperature will not fall off after cooking layered composite film, especially for Ink link for cooking in the composite material, and the vinegar chloride resin with excellent compatibility, the addition of chlorine vinegar resin up to 30% resin binders can dramatically reduce the cost of production of polyurethane composite ink.

Typical product applications:
    For a variety of films, including the PP, PE, PET, PVC, PVDC, nylon, aluminum foil, and a variety of metallized have good adhesion, the chlorine vinegar resin, polyketone resin, cellulose resin and nitrocellulose assisted resin matching well soluble in alcohols, esters, ketones, hydrocarbons and other solvents and mixed solvents in the polyurethane resin compatibility of other foreign countries is very good, can also be formulated ink dissolve each other, dispersed well, membranous, good gloss, high transparency, anti-media capability, the manufacture of plastic and metal film ink ink applied to each of the fine Links Compound ink feed, cooking printing ink, high gloss inks, OPP, PE special ink formulation, the preparation Ink can be applied to flexo, gravure printing, varnish oil use multiple version of a print.

 Product Specifications:
  1. Ingredients: polyurethane resin solution
  2. Appearance: colorless or light-colored transparent liquid
  3. Solid content: (31 ± 1)%
  4. Brookfield Viscosity @ 25 ℃ (cps) :800-1000
  5. Drying of (5-15S, 80 ℃): do not return to stick
  6. Adhesion (adhesive tape stripping test): 90% retention
  7. High temperature resistance: -40 ℃ ≤, ≥ 121 ℃
  8. Solvent composition: fat: alcohol = 80:20