Fiberglass Duct Rudders & Fish tapes
Fiberglass Duct Rodder
Duct Rodders are composed of fiber glass rod which was extruded by fiber glass and high strength resin at high temperature. This type of rod has high tensile strength and flexibility. It was covered by a high density polyethylene engineering plastic as its protect layer, which make duct rodder cover sliding on surface, durable, corrosion resistant and has good insulation performance, which make them safe for use in cable occupied duct.
High Density polyethylene (Grade: for the insulating and jacketing of Telecommunication Cables) is used in the outer diameter coating.
Duct Rodders will equipped with different size reel according to the length of rod. There are wheels on the reel, which make it convenient for moving.
Light weight, durable, resistance to acid, alkali, aging resistant, corrosion resistant.
High tensile strength and bending properties, which make it to go through narrow pipes easily.
Good temperature adaptability, the product will not soften in hot weather / nor become brittle in cold weather. Its usability will not be affected by temperature.
Outer protect layer are made of high density polyethylene engineering plastic, which has good anti-UV capability.
Cover was coated with long-term UV-resistant polyethylene.
Its surface has the advantage of smooth, wear-resistant and long service life.
There are meter marks on the protect layer of duct rodder, which can be used for measuring distance. Marks are printed by professional printing machine, which has the advantage of strong adhesion, clear writing, waterproof, anti-ultraviolet, it can be still clear even after using many times.
There are several kinds of colors for the rod for your chosen.
Technical Data of Duct Rodders
1 - Glass Reinforced Composite core:
General properties
|
Property
|
Value
|
|
Keinforcement
|
E-Glass Fiber
|
|
Glass Content of Inner Part
|
75-80%
|
|
Material of Pulling Rod
|
Epoxy fiber glass (inner)
High density Polyethylene(outer) |
|
Density
|
＞1. 9 gr/cm3
|
|
Diameter Tolerance
|
± 0. 10mm
|
|
Work situation temperature
|
- 40 0C to +800C
|
Mechanical properties
|
Property
|
Value
|
|
Minimum pulling strength
|
4000 N± 5%
|
|
Tensile Modulus
|
＞30000 Mpa
|
|
Consistency of rod
|
150gr/m± 5%
|
|
Flexural Modulus
|
＞30000 Mpa
|
|
Elongation at Break
|
2. 5-3%
|
|
Min. Bending Radius
|
400mm
|
|
Water Absorption
|
＜0. 15% after 24 hr.
|
2 - Polyethylene cover
Material:
Medium Density Polyethylene Resin for the insulating and jacketing of Telecommunication Cables.
|
Property
|
Value
|
|
Tensile Strength
|
＞15N/mm2
|
|
Environmental Stress & crack resistance
|
> 1000 hr.
|
|
Heat Stability
|
OK.
|
|
Carbon Black
|
OK.
|