International Standards:EN760 A AR 1 88 AC H5
GB/T 5293-1999 F5A0-H08A AWS A5.17-2004 F7A0-EL8
Introduction
WD-SJ501 is an agglomerated aluminate-rutile type soldering flux for submerged arc welding with a basicity index of BIIW 0.5. The flux is spherical granular, grain size is from 10 to 60 mesh.It is suited to twin-wire, tandem and multi-wire welding at high speeds, the welding speed is more than 120cm/min. It is particularly useful for welding tube-web-tube joints of finned tubes. It has excellent welding technology properties. Regularly shaped welds are deposited without reduction of area or interface notches. Slag detachability is good, welding blowholes scarcely occur.The special production method ensures that the flux has low moisture pick-up and granular stability. Flux shall be capable of meeting the applied requirements. As the bulk density is low, so is the consumption rate.
Applications
Flat butt and fillet welding of Q345 for steel frames,bridges, spiral pipes, pressure vessel and ships.
Characteristics
It is suited to welding steel plate of less than 10mm. Slag is easy to remove, bead appearance is beautiful, welding defects such as pits and blowholes scarcely occur in high speed fillet welding.
| SiO2+TiO2 | Al2O3+MnO | CaF2 | S | P |
| 35 | 55 | 5 | ≤0.06 | ≤0.08 |
Typical mechanical property of deposited metal
| Matching wire | Yield strength(MPa) | Tensile strength(MPa) | Elongation(%) | Charpy V notch impact strength(J) |
| F7A0-EL8 | ≥400 | 480-650 | ≥ | 0°C ≥ |
| Matching wire | C | Si | Mn | S | P |
| F7A0-EL8 | 0.07 | 0.70 | 1.52 | 0.012 | 0.026 |
Notice:
1. Before welding, flux must be baked for 2 hours at temperature of 300-350°C.
2. Remove rust, oil, moisture and etc. from the weldment.