It features good fineness, large specific surface, good anti-reduction property and high specific inductive capacity. Content of impurities should be strictly controlled. It can be widely used in porcelain capacitor, piezoceramics, transparent electrooptical ceramics etc.
Quality Index Q/JMT005-2008
Item
TiO2,%(m/m)≥98.5
Fe2O3,%(m/m)≤0.08
Sulphur(S),%(m/ m)≤0.06
SiO2,%(m/m)≤0.20
Phosphorus(P),%(m/ m)≤0.05
Al2O3,%(m/m)≤0.10
MgO,%(m/m)≤0.20
K2O+ Na2O,%(m/m)≤0.20
Density%,(g/cm3) ≥3.9
Fineness(45μm residue on sieve),%(m/m)≤0.30
Specific surface(cm2/g),10000~14000
1000°C loss on ignition, %(m/m)≤0.5