BALL CLAY FOR CERAMICS
RTC-BC82: Humidity(%):28±2% Particle size >325 mush:≤1% MOR(kgf/cm2): 30 LOI(%):13.5 Fired Shrinkage(%):6.50 Water Absorption:11.50 Fired Whiteness:82
Al2O3 (%):34.5 Fe2O3 (%):0.85 TiO2(%):0.25
RTC-BC80:Humidity(%):28±2% Particle size >325 mush:≤1% MOR(kgf/cm2): 35 LOI(%):12.8 Fired Shrinkage(%):6.50 Water Absorption:10.0 Fired Whiteness:80
Al2O3 (%):33.5 Fe2O3 (%):0.90 TiO2(%):0.25
RTC-BC78:Humidity(%):28±2% Particle size >325 mush:≤3% MOR(kgf/cm2):40 LOI(%):12.5 Fired Shrinkage(%):5.80 Water Absorption:10.0 Fired Whiteness:78
Al2O3 (%):33.0 Fe2O3 (%):0.95 TiO2(%):0.35
RTC-BC75:Humidity(%):28±2% Particle size >325 mush:≤3% MOR(kgf/cm2):45 LOI(%):12.0 Fired Shrinkage(%):5.80 Water Absorption:9.10 Fired Whiteness:75
Al2O3 (%):32.5 Fe2O3 (%):1.00 TiO2(%):0.35
RTC-BC70:Humidity(%):28±2% Particle size >325 mush:≤3% MOR(kgf/cm2): 45 LOI(%):12.0 Fired Shrinkage(%):5.80 Water Absorption:9.50 Fired Whiteness:70
Al2O3 (%):31.5 Fe2O3 (%):1.05 TiO2(%):0.45
RTC-NT60:Humidity(%):23±2% Particle size >325 mush:≤20% MOR(kgf/cm2): 55 LOI(%):9.15 Fired Shrinkage(%):6.30 Water Absorption:12.20 Fired Whiteness:60
Al2O3 (%):25.0 Fe2O3 (%):1.10 TiO2(%):0.40
RTC-NT55:Humidity(%):23±2% Particle size >325 mush:≤20% MOR(kgf/cm2): 52 LOI(%):8.50 Fired Shrinkage(%):6.30 Water Absorption:12.40 Fired Whiteness:55
Al2O3 (%):22.0 Fe2O3 (%):1.20 TiO2(%):0.40