Stainless steel shot production standards:
We strictly according to Japan JIS standard production stainless steel wire ingredients to production of sandblasting, peen-forming cleaning with stainless steel pill.
Stainless steel shot, with its main technical indices:
|
Product
|
Stainless steel shot
|
|
|
Chemical composition
|
(C)
|
304 austenitic size (304 Austenite Type) : carbon (C) < 0.15%, chromium (Cr) = 16 ~ 18%, Ni (Ni) = 6 ~ 10%, silicon (Si) < 1%,manganese (Mn) < 2%,
430 Type ferritic (430 Ferrite Type) : carbon (C) < 0.15%, chromium (Cr) = 16 ~ 18%, silicon (Si) < 1%, manganese (Mn) < 1%,
410 Type Martensite (410 Martensite Type) : carbon (C) < 0.15%, chromium (Cr) = 11 ~ 13%, silicon (Si) < 1%, manganese (Mn) < 1%
Note: according to can be based on user needs, providing other chemical composition
|
|
(Mn)
|
||
|
(Ｓi)
|
||
|
(Cr)
|
||
|
(Ni)
|
||
|
(S)
|
||
|
(P)
|
||
|
Average hardness
(500g load were determined under)
|
41～59HRC(388～509HV)
|
|
|
Hardness deviation
|
Maximum deviation scope for + 1.0 HRC or + 40HV
|
|
|
Microstructure
|
Longitudinal (Deformed Pearlite)
horizontally (Deformed Pearlite)
|
|
|
Density
|
7.8/cm3
|
|
Note: according to user requirement, offer other chemical composition.
? 304 austenitic size (304 Austenite Type) : carbon (C) < 0.25%, chromium (Cr) = 16 ~ 18%, Ni (Ni) = 6 ~ 10%, silicon (Si) < 1%,
Manganese (Mn) < 2%
? 430 Type ferritic (430 Ferrite Type) : carbon (C) < 0.25%, chromium (Cr) = 16 ~ 18%, silicon (Si) < 1%, manganese (Mn) < 1%
? 410 Type Martensite (410 Martensite Type) : carbon (C) < 0.25%, chromium (Cr) = 11 ~ 13%, silicon (Si) < 1%, manganese (Mn) < 1%
Stainless steel shot of application:
Stainless steel shot blast cleaning: peen-forming cleaning, body.they, non-ferrous alloy, copper alloy, magnesium alloy, zinc alloy die casting cleaning, stainless steel castings peen-forming cleaning, stainless steel forgings peen-forming cleaning, forgings body.they castings rust-removing stainless steel plate cleaning, stainless steel material is clean, stainless steel plate clean, colored pieces as well as surface deburring and light whole enhancement processing, can enhance workpieces the anti-fatigue, corrosion resistance and cover casting surface defects, make product surface whitening and bright.
Sand-removing: stainless steel shot peen-forming derusting, shot peening derusting, casting derusting, forging steel derusting, forging except rust oxide skin, steel derusting, h-beam derusting, steel structure rust.
Stainless steel pill strengthen: stainless steel parts peen-forming aggrandizement, heat-treated pieces shot peening.
Stainless steel bolus shot peening: colored aluminum, copper, magnesian zinc shot peening, die-casting stainless steel shot peening.
Stainless steel shot applicable equipment:
Stainless steel pill is used for peen-forming machine, peen-forming equipment, shot peening machine, shot peening equipment, sandblasting machine, sand blasting equipment, steel pretreatment line, steel pretreatment line, steel structure pretreatment