BALL CLAY FOR CERAMICS

RTC-BC82: Humidity(%):28±2%     Particle size >325 mush:≤1%       MOR(kgf／cm2): 30         LOI(%):13.5        Fired Shrinkage(%):6.50        Water Absorption:11.50   Fired Whiteness:82

Al₂O₃ (%):34.5      Fe₂O₃ (%):0.85     TiO₂(%):0.25

RTC-BC80:Humidity(%):28±2%      Particle size >325 mush:≤1%         MOR(kgf／cm2): 35      LOI(%):12.8        Fired Shrinkage(%):6.50        Water Absorption:10.0   Fired Whiteness:80

Al₂O₃ (%):33.5      Fe₂O₃ (%):0.90     TiO₂(%):0.25

RTC-BC78:Humidity(%):28±2%      Particle size >325 mush:≤3%         MOR(kgf／cm2):40       LOI(%):12.5        Fired Shrinkage(%):5.80        Water Absorption:10.0  Fired Whiteness:78

Al₂O₃ (%):33.0      Fe₂O₃ (%):0.95     TiO₂(%):0.35

RTC-BC75:Humidity(%):28±2%      Particle size >325 mush:≤3%         MOR(kgf／cm2):45       LOI(%):12.0        Fired Shrinkage(%):5.80        Water Absorption:9.10  Fired Whiteness:75

Al₂O₃ (%):32.5      Fe₂O₃ (%):1.00     TiO₂(%):0.35

RTC-BC70:Humidity(%):28±2%      Particle size >325 mush:≤3%         MOR(kgf／cm2): 45      LOI(%):12.0        Fired Shrinkage(%):5.80        Water Absorption:9.50  Fired Whiteness:70

Al₂O₃ (%):31.5      Fe₂O₃ (%):1.05     TiO₂(%):0.45

RTC-NT60:Humidity(%):23±2%      Particle size >325 mush:≤20%       MOR(kgf／cm2): 55      LOI(%):9.15        Fired Shrinkage(%):6.30        Water Absorption:12.20                             Fired Whiteness:60

Al₂O₃ (%):25.0      Fe₂O₃ (%):1.10     TiO₂(%):0.40

RTC-NT55:Humidity(%):23±2%      Particle size >325 mush:≤20%       MOR(kgf／cm2): 52      LOI(%):8.50        Fired Shrinkage(%):6.30        Water Absorption:12.40  Fired Whiteness:55

Al₂O₃ (%):22.0      Fe₂O₃ (%):1.20     TiO₂(%):0.40