Technical Data sheet
|
Typical Values
|
|||||
Fluonine Content %
|
69.0
|
|||||
Specific Gravity
|
1.84
|
|||||
Color
|
wite
|
|||||
Mooney Viscosity ML1+10@121
|
57
|
|||||
Typical Properties of
|
||||||
Test Compound
|
|
|
||||
Polymer
|
|
100
|
||||
MT Black(N990)
|
Phr
|
20
|
||||
MgO
|
Phr
|
3
|
||||
Ca(OH)2
|
Phr
|
6
|
||||
Curing Condition
|
Press
|
10min@170
|
||||
Oven
|
16h@230
|
|||||
Tensile (ASTM D412)
|
MPa
|
15.9
|
||||
Elongation at break (ASTM D412)
|
%
|
278
|
||||
Hardness (ASTM D2240)
|
Shore A
|
74
|
||||
Compression Set (ASTM D395)
|
|
|
||||
Method B ) 200@70h
|
%
|
34.1
|
||||
Typical Rheological Properties
Monsanto Moving Die Rheometer (MDR2000)
100cpm,0.5°Arc,6min@177
|
||||||
ML
|
Nm
|
0.18
|
||||
MH
|
Nm
|
1,07
|
||||
ts2
|
|
1.16
|
||||
t(90)
|
|
3.33
|