4Cr5MoSiV1,H13,Hot work steel
1. Main application
Full hardness,HRC52:54,plastic moulds with high polishing and long service life requirements, such as Bakelite plastic moulds, Tin/lead/Zn and Al alloy die casting mould,such as engine radiator, lights and other decoration products,, Aluminum extruded moulds,such as Aluminum window frame, computer radiator,, hot forging moulds,such as car connecting bar, crank, stainless dinner knife,, Cu alloy extruded, die casting moulds.
2. Manufacturers
Tai Steel
3. Delivery condition
Conventional or ESR, hot rolling or forging, black surface or milling
Hardness: annealed to HB=<229
Width: 305~1000mm Thickness:20~300mm
4. General
ESR steel, high cleanliness, homogeneous microstructure, better heat resistance and toughness; good resistance to high temperature metal abrasion, better high tempering resistance, hardness steady working under 600. low dimensional distortion. good heat:checking resistance, and cold/heat fatigue resistance
5. Chemical analysis
C Si Mn Cr V Mo
0.32~0.45 0.80~1.20 0.20~0.50 4.75~5.50 0.80~1.20 1.10~1.75
6. Delivery
Acc. to your request—Standard steel bar,sawing,
——non:standard steel bar,sawing,
or Mill deliver condition,without sawing or cutting
7. Compared grades,based on usage,
Chinese American German Swedish Japanese
GB AISI DIN ASSAB JIS
4Cr5MoSiV1 H13 1.2344 8407 SKD61
8. Heat treatment ,for reference,
Quenching centigrade degree Tempering centigrade degree/ HRC
1010~1060
centigrade degree 100 200 300 400 500 550 600 650 700
Air/oil or salt bath 52 52 52 54 54 54 50 42 32
mob:+86:15999718496
email:Aliciapeng(at)yahoo.com.cn
MSN:Alicia-steel(at)hotmail.com
Skype:Alicia.Peng
1. Main application
Full hardness,HRC52:54,plastic moulds with high polishing and long service life requirements, such as Bakelite plastic moulds, Tin/lead/Zn and Al alloy die casting mould,such as engine radiator, lights and other decoration products,, Aluminum extruded moulds,such as Aluminum window frame, computer radiator,, hot forging moulds,such as car connecting bar, crank, stainless dinner knife,, Cu alloy extruded, die casting moulds.
2. Manufacturers
Tai Steel
3. Delivery condition
Conventional or ESR, hot rolling or forging, black surface or milling
Hardness: annealed to HB=<229
Width: 305~1000mm Thickness:20~300mm
4. General
ESR steel, high cleanliness, homogeneous microstructure, better heat resistance and toughness; good resistance to high temperature metal abrasion, better high tempering resistance, hardness steady working under 600. low dimensional distortion. good heat:checking resistance, and cold/heat fatigue resistance
5. Chemical analysis
C Si Mn Cr V Mo
0.32~0.45 0.80~1.20 0.20~0.50 4.75~5.50 0.80~1.20 1.10~1.75
6. Delivery
Acc. to your request—Standard steel bar,sawing,
——non:standard steel bar,sawing,
or Mill deliver condition,without sawing or cutting
7. Compared grades,based on usage,
Chinese American German Swedish Japanese
GB AISI DIN ASSAB JIS
4Cr5MoSiV1 H13 1.2344 8407 SKD61
8. Heat treatment ,for reference,
Quenching centigrade degree Tempering centigrade degree/ HRC
1010~1060
centigrade degree 100 200 300 400 500 550 600 650 700
Air/oil or salt bath 52 52 52 54 54 54 50 42 32