| Condition: | New |
|---|---|
| Type: | Hollow Block Making Machine |
| Brick Raw Material: | |
| Processing: | Brick Production Line |
| Method: | Hydraulic Pressure |
| Automatic: | Yes |
| Capacity: | 50000-300000 |
| Place of Origin: | China (Mainland) |
| Brand Name: | Dongyue |
| Model Number: | aac machine |
| Voltage: | 500KW |
| Power: | |
| Dimension(L*W*H): | |
| Certification: | |
| Warranty: | 12 months |
| After-sales Service Provided: | Overseas service center available |
Quick Details
Specifications
Detailed Product Description
AAC Plant Introduce
1. Germany Technology
2. Japan automatic system
3. China local experience
4. ISO9001:2008
AAC PLANT (AUTOCLAVED AERATED CONCRETE) INTRODUCE
1. SIMPLE INTRODUCE
Areated concrete brick (light brick ) is the light and porous buidling material. AAC machine(ww. Chinablockmachinery. Comm) has light keeping temperature cant burn and other advantages. It can be made into many kinds of bricks(for example: 600×200×100,80×80×180,240×115×53,600×200×125), they could be used industry building and common building. They are more and more popular in the world. In the future, they will replace the Clay brick completely.
2. AUTOCLAVED AERATED CONCRETE COMMON CONCEPTION
Common concrete density is usually 1600-2400kg/m3, but Areated concrete are 500kg/m3,600kg/m3,700kg/m3. It has not the big grain, main use silicon material (for example: coal ash, sand, stone dust and others ), through making the material small for example sand, they can be used directly if has enough degree of small (for example coal ash. Mixing calcium material lime cement water to a special slop, then add the aluminum dust and the additive. Make the aluminum dust and the special slop have a Chemical reflect. Then produce Hydrogen to make the concrete slop to expanding or swell, foam. Next, put them into the curing room to concreting cutting steaming curing, last, there will bacome the light brick, the porous rate is 70-80%.
3. ADVANTAGES
light weight
Areated concrete density is usually 400-700kg/m3, (according the market in produce ), same as 1/3 of clay brick and 1/5 common concrete. So use the Light brick can reduce the weight of the build more, and also reduce the beam of roof and pillar press best. Then you can see, it can save the material and cost, it also fighting shaking.
keeping temperature
It has many are porous, the delivery hearting coefficient is 0.9-0.22W/(mk), the same as 1/4 or 1/5 of clay brick, so it is best materials now in the world.
have many kinds material, have lowest waste
Main Material: coal ash sand waste mine material coal stonestone dust and other silicon materials.
4. DETAILED PRODUCT DESCRIPTION
foam block machine,
aerated autoclaved concrete plant, AAC block, aac production line, aac plant, AAC brick, autoclave aerated concrete block, concrete block machine, light weight block
1 Product weight is according to 600kg/m3 to control.
2 annual capacity 200,000M3.
3 set raw material proportion: cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum paste powder 350g/M3.
4 water and material rate 0.631
5 one mould product 2.88M3
6 Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.
7 casting slurry temperature 38-42 degree
8 body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa
9 Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.
10. Cement lime fly ash style aerated block raw material proportion
|
name
|
unit
|
Cement lime fly ash
|
|
flash
|
%
|
65-70
|
|
cement
|
%
|
6-15
|
|
lime
|
%
|
18-25
|
|
gypsum
|
%
|
3-5
|
|
Aluminum powder paste(600kg/m3)
|
1/10000
|
8
|
|
Water & material rate
|
|
0.60-0.65
|
|
Casting system
|
OC
|
36-40
|
|
Aluminum mixing time
|
S
|
30-40
|
11. Cement lime Sand style aerated block raw material proportion
|
Name
|
Unit
|
Cement Lime Sand
|
|
Sand
|
%
|
55-65
|
|
Cement
|
%
|
10-20
|
|
Lime
|
%
|
20-30
|
|
Gypsum
|
%
|
2-3
|
|
Aluminum powder paste(600kg/m3)
|
1/10000
|
8
|
|
Water & material rate
|
|
0.65-0.75
|
|
Casting system
|
OC
|
35-38
|
|
Aluminum mixing time
|
S
|
30-40
|