Chrome Casting Balls
1).No deformation
2).No breaking
3).Lower wear rate longer lasting chromium
2).No breaking
3).Lower wear rate longer lasting chromium
4).Our products have obtained ISO9001:2008 International Quality System Authentication
Executive standard of product GB/T17445-2009Casting balls:
Name
|
Designation
|
Chemical Composition(%)
|
|||||||||
C
|
Si
|
Mn
|
Cr
|
Mo
|
Cu
|
Ni
|
P
|
S
|
|||
Higher Chrome Casting iron Balls
|
ZQCr20
|
2.0-3.0
|
≤1.0
|
0.2-1.5
|
18-22
|
0-2.5
|
0-1.2
|
0-1.5
|
≤0.10
|
≤0.10
|
|
ZQCr15
|
2.0-3.0
|
≤1.0
|
0.2-1.5
|
14-17
|
0-3.0
|
0-1.0
|
0-1.5
|
≤0.10
|
≤0.10
|
||
High Chrome Casting iron Balls
|
ZQCr12
|
2.0-3.0
|
≤1.0
|
0.2-1.5
|
10-14
|
0-1.0
|
0-2.0
|
0-1.5
|
≤0.10
|
≤0.10
|
|
Middle Chrome Casting iron Balls
|
ZQCr7
|
2.1-3.2
|
0.5-2.2
|
0.2-1.5
|
6-10
|
0-1.0
|
0-0.8
|
0-1.5
|
≤0.10
|
≤0.10
|
|
Low Chrome Casting iron Balls
|
ZQCr2
|
2.2-3.6
|
≤1.2
|
0.2-1.5
|
1.0-3.0
|
0-1.0
|
0-0.8
|
_
|
≤0.10
|
≤0.10
|
|
Name
|
Designation
|
Hardness(HRC)
|
AK(j/cm²)
|
Microstructure
|
Times of Falling Balls
|
|
|
||||
Quenched
|
Unquenched
|
|
|
||||||||
High Chrome Casting iron Balls
|
ZQCr20
|
≥56
|
≥45
|
≥4.0
|
M+C
|
≥8000
|
|
|
|||
High Chrome Casting iron Balls
|
ZQCr15
|
≥56
|
≥45
|
≥4.0
|
≥8000
|
|
|
||||
ZQCr13
|
≥56
|
≥49
|
≥4.0
|
≥8000
|
|
|
|||||
Middle Chrome Casting iron Balls
|
ZQCr7
|
_
|
≥48
|
≥4.0
|
|
≥8000
|
|
|
|||
Low Chrome Casting iron Balls
|
ZQCr2
|
_
|
≥45
|
≥4.0
|
|
≥8000
|
|
|
|||