CLC INTRODUCETION:

1. Introduction

Areated concrete block (light block ) is the light and porous buidling material. It has light keeping temperature cant burn and other advantages. It can be made into many kinds of blocks for example: 600×200×100,80×80×180,240×115×53,600×200×125), they could be used industry building and common building. They are more and more popular in the world. In the future, they will replace the Clay block completely. Autoclaved aerated concrete block machine(www, chinablockmachine, net)

2.Areated concrete common conception

Common concrete density is usually 1600-2400kg/m3, but Areated concrete are 500kg/m3,600kg/m3,700kg/m3. It has not the big grain, main use silicon material (for example: coal ash, sand, stone dust and others ), through making the material small for example sand, they can be used directly if has enough degree of small (for example coal ash. Mixing calcium material lime cement water to a special slop, then add the aluminum dust and the additive. Make the aluminum dust and the special slop have a Chemical reflect. Then produce Hydrogen to make the concrete slop to expanding or swell, foam. Next, put them into the curing room to concreting cutting steaming curing, last, there will bacome the light brick, the porous rate is 70-80%.

3. Advantages

1 light weight , Areated concrete density is usually 400-700kg/m3, same as 1/3 of clay block and 1/5 common concrete. So use the Light block can reduce the weight of the build more, and also reduce the beam of roof and pillar press best. Then you can see, it can save the material and cost, it also fighting shaking.

2keeping temperature It has many are porous, the delivery hearting coefficient is 0.9-0.22W/(mk), the same as 1/4 or 1/5 of clay block, so it is best materials now in the world.

have many kinds material, have lowest waste

Main Material: coal ash sand waste mine material coal stonestone dust and other silicon materials.

1 Product weight is according to 600kg/m3 to control.

2 annual capacity 200,000M3.

3 set raw material proportion: cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum paste powder 350g/M3.

4 water and material rate 0.631

5 one mould product 2.88M3

6 Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.

7 casting slurry temperature 38-42 degree

8 body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa

9 Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.

10. Cement lime fly ash style aerated block raw material proportion

name unit Cement lime fly ash
flash % 65-70
cement % 6-15
lime % 18-25
gypsum % 3-5
Aluminum powder paste(600kg/m3) 1/10000 8
Water & material rate0.60-0.65
Casting system OC 36-40
Aluminum mixing time S 30-40
11. Cement lime Sand style aerated block raw material proportion

Name Unit Cement Lime Sand
Sand % 55-65
Cement % 10-20
Lime % 20-30
Gypsum % 2-3
Aluminum powder paste(600kg/m3) 1/10000 8
Water & material rate 0.65-0.75
Casting system OC 35-38
Aluminum mixing time S 30-40

11. Cement lime Sand style aerated block raw material proportion

Reference: cement is 42.5 Portland or 42.5 common cement