Specification :
|
SAMPLE NO.
|
SPECIFICATION
|
|
|
Penetraction Grade
|
MIN.
|
MAX
|
|
Penetraction 25 °c (100g.5s)0.1mm
|
80
|
100
|
|
Penetration (AFTER RTFOT )% of original pen
|
50
|
|
|
Softening Point (Ring and Ball ) °c (NEAT)
|
45
|
52
|
|
Softening Point (R & B) after loss on heating (5hrs 163 °c) °c
|
|
|
|
Softening Point (AFTER RTFOT ) °c
|
45
|
|
|
Flashpoint (Cleveland Open Cup ) °c
|
225
|
|
|
Viscosity at 135°c (VIRGIN ) cst
|
|
|
|
Viscosity at 135°c(AFTER RTFOT) cst
|
CHANGE
|
300%
|
|
Ductility at 25°c cm
|
100
|
|
|
Ductility at 25°c (AFTER rtfot)cm
|
75
|
|
Specification :
|
SAMPLE NO.
|
SPECIFICATION
|
|
|
Penetraction Grade
|
MIN.
|
MAX
|
|
Penetraction 25 °c (100g.5s)0.1mm
|
80
|
100
|
|
Penetration (AFTER RTFOT )% of original pen
|
50
|
|
|
Softening Point (Ring and Ball ) °c (NEAT)
|
45
|
52
|
|
Softening Point (R & B) after loss on heating (5hrs 163 °c) °c
|
|
|
|
Softening Point (AFTER RTFOT ) °c
|
45
|
|
|
Flashpoint (Cleveland Open Cup ) °c
|
225
|
|
|
Viscosity at 135°c (VIRGIN ) cst
|
|
|
|
Viscosity at 135°c(AFTER RTFOT) cst
|
CHANGE
|
300%
|
|
Ductility at 25°c cm
|
100
|
|
|
Ductility at 25°c (AFTER rtfot)cm
|
75
|
|