Welding flux SJ101 Fluoric alkali  sintering solder, with basicity of 1.6-1.8, loose density 1.2-1.25 g/cm3 and grain size 10-60 mesh.

It has excellent performance of anti-hygroscopic, large grain size, low loose density and low consumption. 

Application:

Working with H08MnA, H08MnMo, H10Mn2, H08C;

Used in different kinds of low alloy steel structure.

 

Conform with:AWS A5. 17 EH-14

 

Typical weld metal analysis: (Wt%)

C : 0.05 , Si: 0.23 , Mn : 1.80 , S: 0.022 , P: 0.028

 

Typical Flux Composition Range:

SiO2+TiO2:20-30%, CaO+MgO:25-35%, Al2O3+MnO:20-30%, CaF2:15-25%,8. 

 

Typical weld metal mechanical properties:

Yield stress: ≥400Mpa , Tensible strength :480-660Mpa , Elongation: ≥22% ,

AKV(J)27/ -40deg

 

Packing: Plastic-lined paper bag of 25KG each. 1000kg/pallet10. 

 

Storage:To ensure the integrity of welding flux over an extended period, flux should be stored indoors in a dry place. Moist flux can be redried at300-350°C for 2 hours. Both heating and cooling must be carried out slowly.

 

 