Product Main

Specifications

Ceramic grinding balls are broadly utilized as covering and supporting mterials of 
catalysts in reaction vessels and as packing in towers.They are widely used in 
petrolem chemical ,fertilizer , natural gas and environmental protection industry. With 
stable chemical features and a low rate of water absorption,they can resist high 
temperatures and high pressure,and also can resist the corrosion of acid,alkali and 
some other organic solvents,and can stand the change in temperature during the 
application.Ceramic balls can increase the distribution spots of gas or liquid, and to 
support and protect the activating catalyst with low strength.
The alumina grinding balls has been widely used in ball mills as abrasive media for 
ceramic raw materials and glaze materials in ceramic factories, cement factories, 
enamel factories and glasswork owing to the extraordinarily high density, high hardness,
 high wear resistance. During the abrasive/grinding processes, ceramic balls will not 
broken, it will not contaminate the materials to be grinded. Type: According to the content 
of aluminum oxide: 60-70%, 65-75%, 95%, 95% According to the sizes: Φ25mm-Φ75mm.
Main Specification
Item
High alumina grinding ceramic ball
Middle alumina grinding ceramic ball
Micro-crystal middle-alumina
Carborundum middle alumina
 
92% Al2O3
95% Al2O3
65-75% Al2O3
60-70% Al2O3
Al2O3 (%)
≥92
95
65-75
60-70
SiO2 (%)
3.81
3
20-15
60-70
Fe2O3 (%)
0.06
0.05
0.41
<0.5
TiO2 (%)
0.02
0.04
1.7
1.8
Other (%)
2.53
1.9
5
10
(g/cm3) Bulk density
3.65
3.68
2.93-3.0
2.90-3.0
(%) Water absorption
<0.01
<0.005
<0.01
<0.05
Moh's Hardnes(grade)
9
9
≥8
≥8
Compressium strength
>2000
2100
>1000
>1000
(%) Abrasion
0.01
0.0084
0.02
0.03
colour
White
White
Yellow \ White
Brown
Raw materials
Calcined alumina
Calcined alumina
Refined bauxite powder
Bauxite powder
Forming method
Isostatic pressing
Isostatic pressing
Impact briquetting
Handmade
 
 
 For more details,please don't hesitate to contact with me.