Product Description
Product name: PVC Resin SG1-SG8
Appearance: White powder or white speck,
1. Suspension Method for Production of Polyvinyl Chloride Resin 2. Ethylene-based material 3. Annual productoin: 100, 000MT. 4. ISO9001: 2008 certified factory build in 1984.
UPAC NAME: PVC Resin Polyvinyl Chloride Resin
Formula: [-CH2-CHCl-]
Molecular Weight: 62.4987
CAS: 9002-86-2
HS CODE: 39041010
Properties: It is thermoplastic, insoluble in water, gasoline and ethanol, expandable or soluble in ether, ketone, fatty chlorohy-drocarbons or aromatic hydrocarbons with strong anti--corrosiveness, and good dieletric property.
Polyvinyl chloride can be abbreviated to PVC. It is a kind of thermoplastic plastic.
Specification:
PVC resin - SG1 K-Value 76-75
PVC resin - SG2 K-Value 74-73
PVC resin - SG3 K-Value 72-71
PVC resin - SG4 K-Value 70-69
PVC resin - SG5 K-Value 68-66
PVC resin - SG6 K-Value 65-63
PVC resin - SG7 K-Value 62-60
PVC resin - SG8 K-Value 59-55
PVC resin - S1000 K-Value 68-66
PVC resin - S1300 K-Value 72-71
Application:
SG-1 is used in producing high-grade electrical insulating material
SG-2 is used in producing electrical insulating material, common soft products and film
SG-3 is used in producing electrical insulating materials, agricultural film, daily-use plastic products,
SG-4 is used in producing membranelle for industrial and civil use, tube and pipes
SG-5 is used in producing transparent products section bar, hard tube and decorative materials
SG-6 is used in producing clear foil, hard board and welding rod
SG-7, SG-8 is used in producing clear foil, hard injection molding.
Package, storage and Transportation:
Packed in a kraft paper bag lined with PP-woven bag, Net weight per bag: 25± 0.25kg. Not allowed outdoor storage. Keep away from sunshine and humidity.
1. Suspension Method for Production of Polyvinyl Chloride Resin 2. Ethylene-based material 3. Annual productoin: 100, 000MT. 4. ISO9001: 2008 certified factory build in 1984.
UPAC NAME: PVC Resin Polyvinyl Chloride Resin
Formula: [-CH2-CHCl-]
Molecular Weight: 62.4987
CAS: 9002-86-2
HS CODE: 39041010
Properties: It is thermoplastic, insoluble in water, gasoline and ethanol, expandable or soluble in ether, ketone, fatty chlorohy-drocarbons or aromatic hydrocarbons with strong anti--corrosiveness, and good dieletric property.
Polyvinyl chloride can be abbreviated to PVC. It is a kind of thermoplastic plastic.
Specification:
PVC resin - SG1 K-Value 76-75
PVC resin - SG2 K-Value 74-73
PVC resin - SG3 K-Value 72-71
PVC resin - SG4 K-Value 70-69
PVC resin - SG5 K-Value 68-66
PVC resin - SG6 K-Value 65-63
PVC resin - SG7 K-Value 62-60
PVC resin - SG8 K-Value 59-55
PVC resin - S1000 K-Value 68-66
PVC resin - S1300 K-Value 72-71
Application:
SG-1 is used in producing high-grade electrical insulating material
SG-2 is used in producing electrical insulating material, common soft products and film
SG-3 is used in producing electrical insulating materials, agricultural film, daily-use plastic products,
SG-4 is used in producing membranelle for industrial and civil use, tube and pipes
SG-5 is used in producing transparent products section bar, hard tube and decorative materials
SG-6 is used in producing clear foil, hard board and welding rod
SG-7, SG-8 is used in producing clear foil, hard injection molding.
Package, storage and Transportation:
Packed in a kraft paper bag lined with PP-woven bag, Net weight per bag: 25± 0.25kg. Not allowed outdoor storage. Keep away from sunshine and humidity.
|
Tape:
|
SG1
|
SG2
|
SG3
|
SG4
|
SG5
|
SG6
|
SG7
|
SG8
|
|
K value
|
77-75
|
74-73
|
72-71
|
70-69
|
68-66
|
65-63
|
62-60
|
59-55
|
|
Viscosity, ml/g
|
156-144
|
143-136
|
135-127
|
126-119
|
118-107
|
106-96
|
95-87
|
86-73
|
|
Average polymerization
|
|
|
1350-1250
|
1250-1150
|
1100-1000
|
950-850
|
950-850
|
750-650
|
|
Number of impurity particle≤
|
30
|
30
|
30
|
30
|
30
|
30
|
40
|
40
|
|
Volatiles content %,≤
|
0.40
|
0.40
|
0.40
|
0.40
|
0.40
|
0.40
|
0.40
|
0.40
|
|
Appearing density g/ml≥
|
0.42
|
0.42
|
0.42
|
0.42
|
0.42
|
0.45
|
0.45
|
0.45
|
|
Residual after sieve 0.25mm mesh≤
|
2.0
|
2.0
|
2.0
|
2.0
|
2.0
|
2.0
|
2.0
|
2.0
|
|
0.063mm l≥
|
90
|
90
|
90
|
90
|
90
|
90
|
90
|
90
|
|
Number of
grain/400cm2≤ |
40
|
40
|
40
|
40
|
40
|
40
|
40
|
40
|
|
Plasticizer absorbency value of 100g resin
|
25
|
25
|
25
|
22
|
19
|
16
|
14
|
14
|
|
Whiteness %,≥
|
74
|
74
|
74
|
74
|
74
|
74
|
70
|
70
|
|
Residual chlore thylene content mg/kg≤
|
5
|
5
|
5
|
5
|
5
|
5
|
5
|
5
|
|
Ethylidene chloride mg/kg≤
|
150
|
150
|
150
|
150
|
150
|
150
|
150
|
150
|