Continual quartz  glass  fiber

  Teachnical  specialfections:

   Fiber fineness: 3 ~ 25 μ m

   Purity:more than 99.9 percent content of SiO2

   Performance: Melting point: 1710 ℃

   Crystallization temperature: 700℃ above

   Thermotolerant  performance : 1200 ℃ half hour starts not to change form crisply.

   Thermal coefficient: (mat-like) in the following 200 ℃ <0.03 kcal / m at the degree

                        In 1000 ℃ at 0.2 kcal / m at the degree

   Tensile capacity: 15.4 N

   Tensile strength: normal temperature  > 150Kg/mm2 500 ℃ at the strength reduced by 20%

   Elastic modulus: 96 × 104Kg/mm2

   Dielectric constant: ε = 4.5
Volume Resistance: (for cable)
At room temperature> 1 × 1017 Ω cm
500 ℃ at > 1 × 1010 Ω cm
1000 ℃ at > 1 × 108 Ω cm

   Water tolerance: in the water boiled for three hours without loss

   Acid resistance: 1 NH2SO4 boiled in three hours without loss

   Alkaline resistance: 0.5 NNaOH boiled three hours loss of 0.62 percent

   Applying:

1,   For high-temperature insulation: such as rockets, missiles for insulation, earthquake or other high-temperature insulating materials engineering.

2,   Used for reinforced plastic: high-temperature production of synthetic resin and high-strength glass fiber reinforced plastic materials. Widely used in aviation, missiles and rockets, and so on.

3,   Special cable: use for the foreskin of the cable, used in high temperature on the special-purpose cable.

4,   Acid-base for high-temperature filters

5,   For vacuum  tube  filled with  material: water Rafah as a quartz tube filled with silk material, in order to improve the performance of the tube,and extend the life of vacuum tube