Carbon Steel welding electrodes AWS E6013
1. Name: Mild-steel carbon steel welding electrodes
2. Type: E6011, E6013, E7018, E7016, and others.
3. Specification: 2.5mm*300mm, 3.2 (5)mm*350mm, 4.0mm*400mm, 5.0mm*400mm etc.
4. Welding Current: AC - DC welding current and works well on low voltage AC machines
5. Welding Positions: All positions
6. Packing: 5 kg/box, 4boxes/carton, or 2.5kg/box, 8boxes/carton, or as required
E6013 is suitable for poor fit-up in the joint. It deposits easily and smoothly producing medium to shallow penetration. Small sizes are well adapted to low heat on thin metals.
7. Attention:
1)It requires no heating before using, if welding electrodes is damp, please heating it under the temperature 100 ° C for 30-60 minutes according to the damp situation.
2)Suitable for welding ship building structures such as building and bridges, storage tanks, pipes and pressure vessel fittings.
1. Name: Mild-steel carbon steel welding electrodes
2. Type: E6011, E6013, E7018, E7016, and others.
3. Specification: 2.5mm*300mm, 3.2 (5)mm*350mm, 4.0mm*400mm, 5.0mm*400mm etc.
4. Welding Current: AC - DC welding current and works well on low voltage AC machines
5. Welding Positions: All positions
6. Packing: 5 kg/box, 4boxes/carton, or 2.5kg/box, 8boxes/carton, or as required
E6013 is suitable for poor fit-up in the joint. It deposits easily and smoothly producing medium to shallow penetration. Small sizes are well adapted to low heat on thin metals.
7. Attention:
1)It requires no heating before using, if welding electrodes is damp, please heating it under the temperature 100 ° C for 30-60 minutes according to the damp situation.
2)Suitable for welding ship building structures such as building and bridges, storage tanks, pipes and pressure vessel fittings.
| Chemical Composition Of Metal Deposit | ||||
| C | Mn | Si | S | P |
| ≤ 0.10 | 0.3-0.6 | ≤ 0.35 | ≤ 0.035 | ≤ 0.040 |
| AWS | RM | Rel | A | Akv | ° c |
| A5.1-04 | Mpa | Mpa | % | J | |
| E6013 | ≥ 420 | ≥ 330 | ≥ 17 | 70-130 | 0 |