Specifications:0.3mm——2.0mm

Chemical Composition: 304 Austenite Type  C＜0.15% Cr16~18% Si＜1% Mn＜2% Ni 6~10%

                   430 Ferrite Type     C＜0.15% Cr16~18% Si＜1% Mn＜1% 

                   410 Martensite Type  C＜0.15% Cr11~13% Si＜1% Mn＜1% 

   

Hardness:  308~409HV  32~50HRC

 

Hardness Deviation:  Max Deviation ±3.0HRC

 

Tensile Intensity:  490~1520Mpa

 Durability:  7000 Times

 Microstructure:  304Type: Deformed Austenite  430Type: Deformed Ferrite  410Type: Deformed Martensite   

 Density:  7.8g/cm³

 Bulk Density: 4.5g/cm³