Ceramic Fiber Blanket
KascoTMCeramic Fiber Blanket are formed from high quality Ceramic Fiber Bulk,using melt spinning or blowing process,the fiber being air-laid into a continuous mat and mechanically needled.It's low thermal conductivity,low shrinkage,resistance to chemical erosion(except hydrofluoric acid) and with high tensile strength.It's completely inorganic,so there's no fumes when heating up.
|
Specification
|
| KA-CF-021000 | KA-CF-021260 | KA-CF-021350 | KA-CF-021430 | KA-CF-021500 | KA-CF-021600 | ||
| Temperature(℃) | 1000 | 1260 | 1350 | 1430 | 1500 | 1600 | |
| Color | white | white | white | white | white | white | |
| Fiber Diameter(μm) | 2.6 | 2.6 | 2.6 | 2.8 | 2.65 | 3.1 | |
| Fiber Density(kg/m3) | 2600 | 2600 | 2600 | 2800 | 2650 | 3100 | |
| Density(kg/m3) | 96/128/160 | 96/128/160 | 128 | 96/128 | 128 | 128 | |
| Thermal conductive(W/mK) | 400℃ | 0.09 | 0.07 | —— | —— | —— | —— |
| 600℃ | 0.15 | 0.12 | —— | 0.13 | 0.13 | 0.06 | |
| 800℃ | 0.22 | 0.16 | 0.2 | 0.2 | 0.19 | 0.1 | |
| 1000℃ | —— | —— | 0.28 | 0.29 | 0.26 | 0.14 | |
| Al2O3(%) | 42-44 | 45-47 | 51-53 | 34-36 | 39-41 | 72 | |
| SiO2(%) | 56 | 52-54 | 46-48 | 49.6 | 57-58 | 28 | |
| ZrO2(%) | —— | —— | —— | 14-17 | —— | —— | |
| CrO2(%) | —— | —— | —— | —— | 1.8 | —— | |
| Fe2O3(%) | 0-2 | 0-1 | 0-1 | 0-1 | 0-1 | —— | |
| Shot 212μm≤(％) | 10 | 10 | 10 | 10 | 10 | 1 | |
| Shrinkage(Less than CT200℃*8H) | 2% | 2% | 3% | 2% | 2% | 1% | |
|
Packing
|
| Dimension(MM) | Density(kg/m³) | Packing | |||||||||||||||||
| Thickness | Width | Length | 1000℃ | 1260℃ | 1350℃ | 1400℃ | 1500℃ | 1600℃ | Sheet | Roll | |||||||||
| Sheet | Roll | 96 | 128 | 96 | 128 | 96 | 128 | 96 | 128 | 96 | 128 | 96 | 128 |
Roll
/carton
|
Carton Dimension
(mm)
|
Pcs
/carton
|
Carton Dimension
(mm)
|
||
| 6 | 600 | 1200 |
7200
/3600
|
• | 25 |
1220*620
*155
|
4 |
470*470
*630
|
|||||||||||
| 12.5 | • | • | • | • | • | • | 12 | 2 | |||||||||||
| 20 | • | • | • | • | • | • | 6 | 1 | |||||||||||
| 25 | • | • | • | • | • | • | • | • | • | • | • | 6 | 1 | ||||||
| 50 | • | • | • | • | • | • | • | • | 3 | 1 | |||||||||
|
Applications
• High-temperature kiln and furnace insulation
• Furnace, kiln, reformer and boiler linings • Investment casting mold wrappings • Annealing cover seals • High-temperature filtration • Nuclear insulation applications • Thermal reactor insulation • Expansion joint seals • High-temperature gasketing • Glass furnace crown insulation • Incineration equipment and stack linings |
Characteristics
• Excellent hot strength
• Low thermal conductivity • Low heat storage • Light weight • Resiliency • Thermal shock resistance • High heat reflectance • Excellent thermal stability • Excellent corrosion resistance • Excellent sound absorption • Excellent fire protection |