Niobium Wire
state: Hot rolled, cold drawn, annealed
Diameter: minimum 0.05 mm
Standard: ASTM B392
UNS R04200 Reactor grade unalloyed niobium
UNS R04210 Commercial grade unalloyed niobium
UNS R04251 Reactor grade Niobium-1% zirconium
UNS R04261 Commercial grade u Niobium-1% zirconium
Alloying niobium with 1% zirconium increases the strength of niobium, and decreases slightly its elongation. The increased strength is very advantageous especially at temperatures above 600 °C