Grade

Density

g/cm³

T.R.S

Mpa

Hardness

HRA

Performance & application recommended

ISO

YG6

14.9

2150

90.0

Good wear resistance, used for hard wood and used for proccesing original wood, aluminum section bar, brass rod and cast iron.

K10

YG6A

14.9

1860

92.0

Used for processing hard wood, original wood, alumium section bar, brass rod and cast iron.

K10

YG8

14.7

2320

89.5

Used for proccessing hard wood, soft wood, ferrous and non-ferrous.

K20

YS2T

14.5

2350

92.0

Fine carbide ,high wear resistance, high bending resistance to bonding, high thermal strength. Maching of refractory alloys, stainless steel and high manganese steel, etc.

K10-K20

YS25

13.0

2200

91.0

Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous, metal and non-metallid mateirals.

-

YL10.2

14.5

2150

62.2

Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous, metal and non-metallid mateirals.

K10-K20