Appearance: Yellow red powder, particle size 0.01m, heat resistance, light resistance and strong dyeing power, used in coloring of colored cement roof tile and producing colored cement. The dyeing power is up to 105% and remains bright red after mixing with white cement when used in producing colored cement industry.
S120
Appearance: Yellow red powder, particle size 0.01m, redder than 110 Type, heat resistance, light resistance and strong dyeing power, also used in coloring of colored cement roof tile and producing colored cement.
S130
Appearance: Bright red powder, particle size0.03m, strong dyeing power and ultraviolet radiation absorption property, neutral in pH, used in coloring of colored cement tile and producing colored cement. Because its pH is neutral, it can avoid colored tile salting out and becoming white, and make red tile keep long-term bright appearance when used in coloring of colored cement tile.
S190
Appearance: Violet red powder, exported product, used in producing colored road surface brick, widely used in paint and architectural coating industry, the coloring of rubber and plastic products. Because of its strong hiding power, easy precipitation and water resistance, it is used in paint industry to produce excellent antirust paint, as the substitute of expensive red lead paint.
S120
Appearance: Yellow red powder, particle size 0.01m, redder than 110 Type, heat resistance, light resistance and strong dyeing power, also used in coloring of colored cement roof tile and producing colored cement.
S130
Appearance: Bright red powder, particle size0.03m, strong dyeing power and ultraviolet radiation absorption property, neutral in pH, used in coloring of colored cement tile and producing colored cement. Because its pH is neutral, it can avoid colored tile salting out and becoming white, and make red tile keep long-term bright appearance when used in coloring of colored cement tile.
S190
Appearance: Violet red powder, exported product, used in producing colored road surface brick, widely used in paint and architectural coating industry, the coloring of rubber and plastic products. Because of its strong hiding power, easy precipitation and water resistance, it is used in paint industry to produce excellent antirust paint, as the substitute of expensive red lead paint.
|
item |
Iron oxide red (110, 120, 130) |
Iron oxide green |
Iron oxide brown |
Iron oxide black |
Iron oxide yellow |
Iron oxide blue |
|
Fe2o3/fe3o4≥ % |
96 |
- |
92 |
93 |
86 |
- |
|
105' C moisture ≤ % |
1.0 |
1.0 |
1.0 |
1.0 |
1.0 |
1.0 |
|
Water soluble salts ≤ % |
0.3 |
0.5 |
0.5 |
0.5 |
0.3 |
0.5 |
|
Residue on 45um ≤ % |
0.2 |
0.3 |
0.30 |
0.30 |
0.3 |
0.3 |
|
PH-value |
3.5-8 |
3-7 |
4-7 |
5-8 |
3.5-7 |
3-7 |
|
Oil absorption |
15-25 |
15-25 |
20-30 |
15-25 |
25-35 |
15-20 |
|
Tinting strength% |
95-105 |
95-105 |
95-105 |
95-105 |
95-105 |
95-105 |
|
Density approx/cm3 |
0.7-1.1 |
0.4-0.8 |
0.8-1.3 |
0.9-1.2 |
0.4-0.6 |
|