Model: High Form Crucibles | ||||||||
Alumina Crucibles are manufactured for more than 20 years and have a skill production technology in different shapes and range of sizes from few milliliters to several liters, these fully dense, high purity an high temperature use,fine grain products find use in a range of high temperature applications such as metal processing / molten glass, rapid thermal cycling, gemstone purification for jewelry industry etc. Majodrity of applications require the ceramic to be impervious, porous forms can also be made on order. | ||||||||
Main Specifications: | ||||||||
Property: Purity:≥99.6% Density:3.85g/cm3 Compressive Strength:2500Mpa Flexural Strength: 360Mpa Thermal Shock : good Max service temperature: 1800C |
||||||||
Specification and Range of Resistance: | ||||||||
Type | Capacity (ml) | Top Out Diameter | Bottom Out Diameter | Out Height | ||||
XY-A1-6 | 5 | in | mm | in | mm | in | mm | |
0.98202 | 25 | 0.59 | 15 | 1.1 | 28 | |||
XY -A1-11 | 10 | in | mm | in | mm | in | mm | |
1.14 | 29 | 0.71 | 18 | 1.34 | 34 | |||
XY -A1-20 | 20 | in | mm | in | mm | in | mm | |
1.42 | 36 | 0.91 | 23 | 1.61 | 41 | |||
XY -A1-30 | 30 | in | mm | in | mm | In | mm | |
1.5 | 38 | 0.98 | 25 | 1.77 | 45 | |||
XY -A1-50 | 50 | in | mm | in | mm | in | mm | |
1.89 | 48 | 1.18 | 30 | 2.05 | 54 | |||
XY -A1-100 | 100 | in | mm | in | mm | in | mm | |
2.28 | 58 | 1.38 | 35 | 2.68 | 68 | |||
XY -A1-150 | 150 | in | mm | in | mm | in | mm | |
2.6 | 68 | 1.57 | 40 | 3.15 | 80 | |||
XY -A1-200 | 200 | in | mm | in | mm | in | mm | |
2.87 | 73 | 1.73 | 44 | 3.38 | 86 | |||
XY -A1-250 | 250 | in | mm | in | mm | in | mm | |
3.11 | 75 | 1.65 | 46 | 3.66 | 95 | |||
XY -A1-300 | 300 | in | mm | in | mm | in | mm | |
feature | ||||||||
1. High purity: Al2O3>99.7%, high chemical etching resistance; 2. Temperature tolerance, at 1600C for long term application, and at 1800C for short term application 3. Resistant to sudden cold and hot, un-explosive 4. High density of slip casting |
||||||||
Product description: | ||||||||
Name | Square alumina crucible | |||||||
Chemical ingredient | Al2O3 | ≥99.6 | ||||||
R2O | ≤0.2 | |||||||
Fe2O3 | ≤0.1 | |||||||
SiO2 | ≤0.2 | |||||||
Volume density (g/cm2) | ≥3.80 | |||||||
Apparent porosity (%) | <1 | |||||||
Bending strength (Mpa) | >350 | |||||||
Compression strength (Mpa) | >12000 | |||||||
Dielectric constant ∑(1MHz) | 2 | |||||||
Max. service temperature (C) | 1800 |