Cold work mould steel Cr12
High hardness and high wear resistance
use for various complicated cold work die
High hardness and high wear resistance
use for various complicated cold work die
Cold work tool steel AISI D3 /DIN1.2080/JIS SKD1/GB Cr12
Feature: High hardness and high wear resistance with little deformation.
Application: Various complicated cold work dies, such as cold punch Die, pins, drawing dies, plate dies and edge or cold shears.
Application: Various complicated cold work dies, such as cold punch Die, pins, drawing dies, plate dies and edge or cold shears.
1.Chemical Composition
Standard
|
Steel Grade
|
C
|
Si
|
Mn
|
P≤
|
S≤
|
Cr
|
Mo
|
V
|
W
|
other
|
DIN
|
1.2080
|
1.90-2.20
|
0.10-0.40
|
0.15-0.45
|
0.030
|
0.030
|
11.00-12.00
|
|
|
|
|
ASTM
|
D3
|
2.00-2.35
|
0.10-0.60
|
0.20-0.60
|
0.030
|
0.030
|
11.0-13.5
|
|
≤1.00
|
≤1.00
|
|
GB
|
Cr12
|
2.00-2.30
|
≤0.40
|
≤0.40
|
0.030
|
0.030
|
11.50-13.00
|
|
|
|
|
Size
Round
|
Diameter
|
Length
|
|
10mm-260m
|
2000mm-5800mm
|
||
Steel plate
|
Thickness
|
Width
|
Length
|
12-70mm
|
155-610mm
|
2000mm-6000mm
|
3.Hardness of annealed:
HBS≤250
|
4. The Process
EAF+LF+VD+ESR+Forged or hot rolled+Heat Treatment(optional)
|
6)Performance:
1. Widely-used cold-work die steel is a high-carbon and high-chromium type of ledeburite steel.
2. Having good hardenability and abrasive resistance, with small quenching distortion.
3. Having bad impact toughness, it is brittle and it is easy to form uneven eutectic carbides.
(7)Applications:
1. It is mainly used for manufacture of cold-work dies, punches, cold cutting scissors, drill bushes, gauges, wire-drawing dies, coining dies, draw bench boards, drawing dies, thread rolling dies, etc. with high abrasive resistance and small shock load.
2. It is used for processing of cutters made of materials which are not hard.
3. It is used for plastic moulds with high abrasive resistance and long service life.