Ceramic Structured Packing is made up of many packing unit bodies that share the same geometry shape. Corrugated ceramic packing is called Kelapak packing abroad,it is also called high efficiency packing,because its separation-efficiency is several times to more than ten times of loose cops packing.Compared with loose cops plate tower packing.Corrugated plate ceramic packing has a great number of advantages such as high-efficiency, large thruput,low liquid holdup,unsharp amplification and good operability.
Advantage:
●The most economical range is F-factor 1.5-2.0
●Pressure drop of each theoretical sheet is 0.3-1 mbar
●Minimum liquid load is 2001/m2h
●A distributor should be installed for evry 3-4 meters inside packing towers with diameters of more than 300 mm
Application:
●Fining process of corrosive mixtures, which have strict requirements for pressure drop and number of theoretical sheets.
●Vacuum treatment under absolute pressure higher than 1 mbar.
●Fining and distillation of halogen organic compounds.
Main specification:
|
Type
|
Specific Surface Area
m2/m3
|
Corrugated
Plate thickness mm
|
Heaping weight
Kg/m3
|
Void
Volume
%
|
Pressure
Drop mmHg/m
|
Theoretical
Pieces
m-1
|
Liquid
Load m3/m2h
|
Max
Factorm/s (kg/m3)
-1
|
|
100Y
|
100
|
2.5±0.5
|
300
|
87.5
|
1.6
|
1
|
0.2-100
|
3.2
|
|
125Y
|
125
|
2.5±0.5
|
330
|
85
|
1.8
|
1-1.5
|
0.2-100
|
3.0
|
|
160Y
|
160
|
2.2±0.5
|
370
|
84
|
2
|
1.5-2
|
0.2-100
|
2.8
|
|
250Y
|
250
|
1.4±0.5
|
420
|
80
|
2
|
2.2
|
0.2-100
|
2.6
|
|
350Y
|
350
|
1.2±0.5
|
470
|
78
|
2.5
|
2.8
|
0.2-100
|
2.5
|
|
400Y
|
400
|
1.2±0.2
|
500
|
75
|
3
|
3
|
0.2-100
|
2.0
|
|
450Y
|
450
|
1.0±0.2
|
520
|
72
|
4
|
4
|
0.2-100
|
1.8
|
|
550Y
|
550
|
0.8±0.2
|
620
|
74
|
5.5
|
5-6
|
0.18-100
|
1.4
|
|
700Y
|
700
|
0.8±0.2
|
650
|
72
|
6
|
7
|
0.15-100
|
1.3
|
|
100X
|
100
|
2.5±0.5
|
280
|
92
|
1.5
|
1
|
0.2-100
|
3.5
|
|
125X
|
125
|
2.2±0.5
|
300
|
90
|
1.8
|
1.5
|
0.2-100
|
3.2
|
|
160X
|
160
|
1.4±0.5
|
350
|
85
|
2
|
1.8
|
0.2-100
|
3.0
|
|
250X
|
250
|
1.2±0.5
|
380
|
80
|
2.5
|
2.3
|
0.2-100
|
2.8
|
|
350X
|
350
|
1.2±0.5
|
450
|
78
|
3
|
2.5
|
0.2-100
|
2.6
|
|
400X
|
400
|
1.2±0.2
|
480
|
75
|
4
|
2.8
|
0.2-100
|
2.2
|
|
450X
|
450
|
1.0±0.2
|
500
|
72
|
4.5
|
3-4
|
0.2-100
|
2.0
|
|
470X
|
470
|
1.0±0.2
|
440
|
75
|
5
|
5
|
0.2-100
|
1.8
|
|
550X
|
550
|
0.8±0.2
|
620
|
74
|
5.5
|
5-6
|
0.18-100
|
1.4
|
|
700X
|
700
|
0.8±0.2
|
650
|
72
|
6
|
7
|
0.15-100
|
1.3
|
Chemical Specification:
|
SiO2
|
Al2O3
|
Fe2O3
|
CaO
|
MgO
|
Other
|
|
≥72%
|
≥23%
|
≤0.5%
|
≤1.0%
|
≤0.1%
|
2.0%
|
Physical Properties:
|
Specific weight
|
Water adsorption
|
Acid resistance
|
Crushing strength
|
Operation temperature
|
Moh’s hardness
|
Ignition lost
|
|
2.5g/cm3
|
≤0.5%
|
>99.5%
|
≤1000℃
|
≥130Mpa
|
≥7
|
≤5.0%
|