A-286 alloy is an age-hardenable iron base superalloy for applications requiring high strength from -320°F up to 1000°F long time, 1300-1500°F short time. Oxidation resistance is high for continuous service to 1500°F, intermittent to 1800°F. Aqueous corrosion resistance is comparable to 316/316L stainless. Heat treatment according to AMS 5525 requires a solution anneal at 1800°F, air cool. Age at 1325°F for 16 hours and then air cool.
Common Trade Names
A286 Stainless, A286 Alloy
Inventory
A-286 Sheet, A-286 Coil, A-286 Round Bar, A-286 Hex Bar
Specifications
UNS S66286, Werkstoff 1.4980, EN 1.4980
AMS: 5525, 5804, 5732, 5737
GE B50T1181, GE B50T12, GE B50T81
Chemical Composition, %
 
Cr
Ni
Mo
Co
Va
Al
Ti
B
C
Fe
Mn
Si
Ph
S
MIN
13.5
24.0
1.0
-
0.1
-
1.9
0.003
-
-
-
-
-
-
MAX
16.0
27.0
1.5
1.0
0.5
0.35
2.35
0.01
0.08
Balance
2.0
1.0
0.025
0.025
Features
· High strength to 1000°F
· Oxidation resistant to 1500°F
Applications
· Jet engine components
· High temperature fasteners, springs
· Non-magnetic cryogenic equipment
Physical Properties
Density: 0.303 lb/inch3 
Melting Range: 2350-2460°F
Temperature, °F
200
800
1000
1200
1400
Coefficient of Thermal Expansion, in/in°F x 10-6
9.2
9.6
9.8
9.9
10.3
Thermal Conductivity
Btu • ft/ft2 • hr • °F
8.0
9.8
13.0
14.1
-
Modulus of Elasticity,
psi X 106
-
-
24
22
23
* 70°F to indicated temperature.
Mechanical Properties
Representative Tensile Properties, Sheet
Temperature, °F
70*
70
400
800
1000
1200
1400
Ultimate Tensile Strength, ksi
95*
145
143
138
131
103
64
0.2% Yield Strength, ksi
50*
95
93
93
87
88
62
Elongation, %
40*
24
21
18
18
13
18
* Annealed
Typical Stress-Rupture Strength 1800°F/1325°F Heat Treat
Temperature, °F
1000
1100
1200
100 Hours, ksi
99
81
61
1,000 Hours, ksi
88
71
46