Structure
|
All-glass double-tube co-axial structure
|
||
Glass material
|
High borosilicate 3.3 glass
|
||
External pipe diameter and thickness
|
dia.=47±0.7mm &=1.6mm
dia.=58±0.7mm &=1.6mm
dia.=70±0.7mm &=0.2mm
|
||
Internal pipe diameter and thickness
|
dia.=37±0.7mm &=1.6mm
dia.=47±0.7mm &=1.6mm
dia.=58±0.7mm &=1.6mm
|
||
Pipe length
|
1500 1600 1700 1800 1900 2000 2100mm
|
||
Absorptive coating property
|
Structure
|
Cu/ss-aln(h)/ss-aln(L)/aln
|
|
Sediment method
|
3 target magnerton sputtering plating
|
||
Specific absorption
|
as=0.90~0.93(AM1.5)
|
||
Emission ratio
|
0.05~0.075 (80℃±5℃)
|
||
Vacuum tightness
|
P≤5.0×10-³Pa
|
||
Idle sunning property parameters
|
Y=260~300㎡℃/KW
|
||
Solar irradiation for obtaining a preset water temperature
|
H≤4.7MJ/㎡
|
H=3.7~4.2MJ/㎡
|
|
H≤3.7MJ/㎡
|
H=2.9~3.2MJ/㎡
|
||
Average heat loss coefficient
|
Ult=0.4~0.6W/(㎡℃)
|
||