Material Name: High quality carbon structural steel
Grade: 55
Standard: GB / T 699-1999
● Features and Scope:
High-strength carbon steel, treated with high surface hardness and strength. Generally used for high surface hardness and strength after normalizing or quenching.
● Chemical Composition:
C: 0.52 ~ 0.60,  Si: 0.17 ~ 0.37,  Mn: 0.50 ~ 0.80,  S: ≤ 0.035
P: ≤ 0.035,  Cr: ≤ 0.25,   Ni: ≤ 0.25,  Cu: ≤ 0.25
● Mechanical Properties:
Tensile strength σb (MPa): ≥ 645 (66)
Yield strength σs (MPa): ≥ 380 (39)
Elongation δ5 (%): ≥ 13
Reduction of area ψ (%): ≥ 35
Hardness: no heat treatment, ≤ 255HB; annealed steel, ≤ 217HB
Sample Size: Sample size is 25mm
● Heat treatment and microstructure specifications:
Heat treatment specifications: normalizing, 820 ℃; quenching, 820 ℃; tempering, 600 ℃.