SiO2 (%) ≥	94	95	94
Al2O3,(%)  ≤	1.2		1.0
Fe2O3 (%) ≤	1.3	1.2	1.5
Refractoriness (C) ≥	1710	1710	1710
Refractoriness under load 0.2 MPa (C),≥	1650	1650	1650
True density (g/cm3) ≥	2.34	2.33	2.37
Apparent porosity(%) ≤	22	19	22
Cold crushing strength (MPa) ≥	30	35	30
Residual quartez (%) ≤	1		1
Linear change after reheating 1450C×2h  (%)	+0.2		+0.2