Application:
ER316/ER316L: 10Cr-12Ni-2.5Mo (SUS316) used for welding steel, as well as operating Temperature of 600~750 ℃ chemical, oil refining tube heat exchangers, furnace tubes Peter. Arc stability, weld appearance. Anti-oxidation temperature not less than 870 ℃.
ER316LSi: Primarily used for welding of high silicon, low carbon , 18Cr - 12Ni - 2.5Mo steels.
Conform with: AWS:ER316 YB/T:H0Cr19Ni12Mo2 JIS:Y316
AWS:ER316L YB/T:H0Cr19Ni12Mo2 JIS:Y316L
AWS:ER316LSi JIS:Y316LSi
|
| Wire Type | Wire Size | Spool Size | Net Weight |
| MIG Wire | φ0.8~1.6(mm) | D100mm D200mm D300mm D270mm | 1kg 5kg 15kg 20kg |
| TIG Wire | φ1.6~5.0(mm) | 1 meter | 5kg 10kg |
| chemical composition of welding wire(%) | |||||||||
| Type | Mechanical Properties or Deposited Metal | C | Si | Mn | Cr | Ni | Mo | other | |
| Tensile strengthσb(Mpa) | Elongationδ5(%) | ||||||||
| ER316 | 578 | 38 | 0.050 | 0.60 | 1.78 | 19.61 | 12.50 | 2.20 | - |
| ER316L | 590 | 40 | 0.025 | 0.42 | 1.91 | 19.10 | 12.58 | 2.57 | - |
| ER316LSi | 562 | 31 | 0.021 | 0.77 | 1.95 | 19.20 | 13.45 | 2.58 | - |
| Please be noted | Welding position | ||
|
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust. Before welding please clean out the oil,rust,water etc from the work parts |
|||