E501T-1, E71T-1 Use is CO2 flux cored wire for welding titanium. High deposition efficiency, excellent all-position welding performance can also be vertical down welding. For ships, pressure vessels, mechanical equipment, steel bridges, steel low carbon steel and 490MPa grade high strength steel welding. Standard: GB / T: E501T-1 AWS: E71T-1

Package	Specification	Silk panel	Net weight
	Φ1.0~1.6(mm)	D100mm D200mm D270mm D300mm K300mm	1 kg, 5 kg, 15 kg, 18 kg, 20 kg

Chemical Wire Element(%)	C	Mn		Si		P		S
	≤0.10	≤1.75		≤0.75		≤0.03		≤0.03
Deposited metal Mechanical properties	Yield strengthσ0.2(Mpa)		Tensile strengthσb(Mpa)		Elongationδ5(%)		AKV Impact Energy(J)
	≥400		≥480		≥22		≥47(0℃)		≥47(-20℃)

Wire diameter(mm)	Φ1.0	φ1.2	φ1.4	φ1.6	Welding position
Welding current(AMP.)	80~250	120~300	160~400	190~450
Notes:	1 wire into the plant must be stored in a dry environment, not just open the disk waterproof wire welding package 2 should be removed before welding surface of the oil, rust, moisture and other impurities 3. The use of CO2 gas, CO2 gas purity of 99.98%. 4 CO2 protection welding gas flow should be controlled in 20-25L/min. 5 out of wire length should be controlled at 15-25mm range. 6 to be preheated before welding to 150-300 ℃, after welding to be tempered by 700-740 ℃.