1. 3.7v li-po battery
2. Japan Seiko PCM
3. No memory effect
4: UL, CE, RoHs, Reach
2. Japan Seiko PCM
3. No memory effect
4: UL, CE, RoHs, Reach
TYPE: 3.7v li-po battery 4100mAh New Model can be ready in 15 days
High-energy Density
Low-self-discharge
Chargeable up to 500 or 1,000 times
Low-internal resistance
Item
|
Rated performance
|
Note
|
Normal Voltage
|
3.7V
|
|
Normal Capacity
|
4100mAh
|
Discharge:0.2C
|
Charge Voltage
|
4.20±0.05V
|
|
Charge Current
|
54mA
|
Standard Charge:0.2C
|
Max Charge Current
|
410 mA
|
1CmA
|
Max Discharge Current
|
410mA
|
1CmA
|
Charge Method
|
CC/CV
|
Constant Current
Constant Voltage
|
Discharge cut-off voltage
|
3.0V
|
|
Operating Temperature
|
0~ +450C
|
Charge
|
-20~ +450C
|
Discharge
|
|
Storage Temperature
|
-20~ +450C
|
Less than 1 month
|
-20~ +350C
|
More than 6 months
|
|
Weight
|
About: 6g
|
|
Reliability
Item
|
Conditions and others
|
Requirement
|
||
Temperature performance
|
Cell shall be meet the discharge capacity requirements listed in the below table under respective discharge temperatures. The capacities are to be measured with constant discharge current 0.2C (3.0V cut-off) after standard charge at 25±20C.
|
|
||
Discharge Temperature
|
||||
-200C
|
250C
|
600C
|
||
50%
|
100%
|
95%
|
||
Vibration
|
After standard charge, the battery is to be tested as following conditions:
Amplitude: 0.8mm
Frequency: 10~55Hz(sweep: 1Hz/min)
Direction: X/Y/Z axis for 90~100min. The battery is to be tested in three mutually perpendicular to each axis.
|
No fire, no explosion, no smoking is obtained
|
||
Short Circuit Test
|
After standard charge, the battery is to be short-circuited by connecting the positive and negative terminals of the battery with copper wire having a maximum resistance load of 0.1Ω.
|
No explosion, no fire. The temperature of the exterior cell casing shall not exceed 130°C
|
||
Drop Test
|
Drop the battery in the shipment condition(full-charge) from 1m height onto 5cm or thicker concrete with p-tile on it 3 times each of X, Y, and Z directions at 25±20C.
|
No fire, no explosion, no smoking is obtained.
|
||
Cycle life
|
Test condition:
Charge:0.5C to 4.2V
Discharge:0.5C to 3.0V
80% or more of 1st cycle capacity at 0.5C discharge of Operation
|
≥500Cycles
|
||
Storage
Characteristics
|
1. Standard charge at 23±5°C.
2. The battery shall be stored at 60±5°C for 7days and rested at room temperature for 1 hour then measured with constant discharge current 0.2C with 3.0V cut-off.
|
Retained Capacity
≥85%
|