Grades 7050 9050k 9020 7042 1802
MFR g.10min 2.0 1.9 1.9 2.0 2.0
Density g.cm3 0.923 0.920 0.922 0.920 0.920
Tensile Strength at yield MPa>= 8 8.3 8.3 10 10
Tensile Strength at break MPa>= 12 12 12 16 -
Elongation at break %<= 500 500 500 750 750
Haze %<= 14 17 - 12 12
Fish Eyes pcs.1520cm3 0.8mm<=8 2 2 2 2
0.4mm<=40 15 15 10 10
Certifications - - - ROHS ROHS
Grades 7042 7042 7042 2001
MFR g.10min 2.0 2.0 2.0 2.0
Density g.cm3 0.920 0.920 0.918. 0.920
Tensile Strength at yield MPa>= 8.3 8 8 8
Tensile Strength at break MPa>= 12 12 12 12
Elongation at break %<= 500 - 550 500
Haze %<= - 15 14 20
Fish Eyes pcs.1520cm3 0.8mm<=- - 2 2
0.4mm<= - - 15 15
Certifications
Grades 9088 9085 QLLP01 1801
MFR g.10min 0.8 0.7 1.0 1.0
Density g.cm3 0.920 0.920 0.920 0.918
Tensile Strength at yield MPa>= 8.3 8.3 7 8
Tensile Strength at break MPa>= 12 17 15 -
Elongation at break %<= 500 500 500 650
Haze %<= 13 - - 14
Fish Eyes pcs.1520cm3 0.8mm<=8 8 - 8
0.4mm<=40 40 - 40
Certifications - - - ROHS